Nanographene-Au fine-tuning to intensify plasmonic-resonance of polymeric hybrid bionanosystem for synergistic phototherapy and nerve photobiomodulation.

Here, we report the multi-photo-bioactivity of the plasmonic-nano graphitic coordinated polycaprolactone-based aligned nanofibrous scaffolds-based bionanosystem for photothermal breast and colon cancer therapies and peripheral nerve photobiomodulation. The size-optimized colloidal reduced graphene oxide (nRGO, 180 nm) nanosheets, for enhanced photothermal impact, were surface-functionalized with gold nanospheres (AuNPs) to prepare the nRGO@AuNP monodispersed nano-composite and then doped 2.0 mg of nRGO@AuNP in biocompatible and biodegradable polymer polycaprolactone (PCL) to fabricate the nRGO@AuNP-PCL (2.0 mg) plasmonic aligned nanofibrous scaffolds. More than 90% of cancer cells, breast cancer (MCF-7) as well as colon cancer (CT-26), ablated after 5 min of low NIR (808 nm) laser power (0.72 W/cm2 ) illumination with nRGO@AuNP-PCL (2.0 mg) aligned nanofibrous scaffolds. Besides, the nRGO@AuNP-PCL (2.0 mg) provided an extraordinary microenvironment for adhesion, nerve growth, proliferation, and differentiation of PC12 and S42 cells which mimics the natural extracellular matrix. The 2.5-fold increase in neurite length was observed with NIR illumination after 3 days whereas 1.7-fold was found without NIR illumination after 7 days in comparison to PCL (pure). The current findings will be useful to provide a new crucial approach for preparing biocompatible multifunctional composite plasmonic nanofibers as a highly efficient distinct platform for photothermal therapies and promising bioimplants to overcome the loss of sensation after cancer surgery through nerve photobiomodulation.