Synthesis and Transport Properties of ZnSnP 2-y As y Chalcopyrite Solid Solutions.
Materials 2024 April 10
This work focuses on the synthesis and properties of quaternary ZnSnP2-y Asy chalcopyrite solid solutions. Full miscibility of the solid solution is achieved using ball milling followed by hot press sintering. The measured electrical conductivity increases substantially with As substitution from 0.03 S cm-1 for ZnSnP2 to 10.3 S cm-1 for ZnSnAs2 at 715 K. Band gaps calculated from the activation energies show a steady decrease with increasing As concentration from 1.4 eV for ZnSnP2 to 0.7 eV for ZnSnAs2 . The Seebeck coefficient decreases significantly with As substitution from nearly 1000 μV K-1 for ZnSnP2 to -100 μV K-1 for ZnSnAs2 at 650 K. Thermal conductivity is decreased for the solid solutions due to alloy phonon scattering, compared to the end members with y = 0 and y = 2, with the y = 0.5 and y = 1.0 samples exhibiting the lowest values of 1.4 W m-1 K-1 at 825 K. Figure of merit values are increased for the undoped solid solutions at lower temperatures when compared to the end members due to the decreased thermal conductivity, with the y = 0.5 sample reaching zT = 1.6 × 10-3 and y = 1 reaching 2.1 × 10-3 at 700 K. The largest values of the figure of merit zT for the undoped series was found for y = 2 with zT = 2.8 × 10-3 at 700 K due to the increasing n -type Seebeck coefficient. Boltztrap calculations reveal that p -doping could yield zT values above unity at 800 K in case of ZnSnAs2 , comparable with ZnSnP2 .
Full text links
Related Resources
Trending Papers
Obesity pharmacotherapy in older adults: a narrative review of evidence.International Journal of Obesity 2024 May 7
SGLT2 Inhibitors in Kidney Diseases-A Narrative Review.International Journal of Molecular Sciences 2024 May 2
Use of Intravenous Albumin: A Guideline from the International Collaboration for Transfusion Medicine Guidelines.Chest 2024 March 5
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app
All material on this website is protected by copyright, Copyright © 1994-2024 by WebMD LLC.
This website also contains material copyrighted by 3rd parties.
By using this service, you agree to our terms of use and privacy policy.
Your Privacy Choices
You can now claim free CME credits for this literature searchClaim now
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app