Flexural strength of repaired denture base materials manufactured for the CAD-CAM technique.
Journal of Oral Science 2024 March 16
PURPOSE: To evaluate the flexural properties of repaired poly(methylmethacrylate) (PMMA) denture base materials for computer-aided design/computer-aided manufacturing (CAD-CAM) and to compare them with heat-activated polymerized PMMA.
METHODS: A total of 288 specimens (65 × 10 × 2.5 mm) were prepared using both CAD-CAM and conventional blocks and repaired using autopolymerizing and visible-light polymerizing (VLC) materials. Microwave energy, water storage and hydroflask polymerization were applied as additional post-polymerization cycles after the repair process. The flexural strength (FS) of the specimens was evaluated using the three-point bending test. Data were evaluated statistically using 2-way ANOVA followed by Bonferroni's correction to determine the significance of differences between the groups (P ≤ 0.05).
RESULTS: The FS of the denture base materials for CAD-CAM was significantly higher than that for the heat-activated group (P ≤ 0.05). The FS was significantly highest when microwave energy was used for the post-polymerization cycle. The FS values for all groups repaired with VLC resin were significantly lower than for the autopolymerization group (P ≤ 0.05).
CONCLUSION: The flexural properties of denture base materials for CAD-CAM repaired using autopolymerizing acrylic resins can recover by 50-70%. Additional post-polymerization cycles for autopolymerizing repair resin can be suggested to improve the clinical service properties of repaired dentures.
METHODS: A total of 288 specimens (65 × 10 × 2.5 mm) were prepared using both CAD-CAM and conventional blocks and repaired using autopolymerizing and visible-light polymerizing (VLC) materials. Microwave energy, water storage and hydroflask polymerization were applied as additional post-polymerization cycles after the repair process. The flexural strength (FS) of the specimens was evaluated using the three-point bending test. Data were evaluated statistically using 2-way ANOVA followed by Bonferroni's correction to determine the significance of differences between the groups (P ≤ 0.05).
RESULTS: The FS of the denture base materials for CAD-CAM was significantly higher than that for the heat-activated group (P ≤ 0.05). The FS was significantly highest when microwave energy was used for the post-polymerization cycle. The FS values for all groups repaired with VLC resin were significantly lower than for the autopolymerization group (P ≤ 0.05).
CONCLUSION: The flexural properties of denture base materials for CAD-CAM repaired using autopolymerizing acrylic resins can recover by 50-70%. Additional post-polymerization cycles for autopolymerizing repair resin can be suggested to improve the clinical service properties of repaired dentures.
Full text links
Related Resources
Trending Papers
A Guide to the Use of Vasopressors and Inotropes for Patients in Shock.Journal of Intensive Care Medicine 2024 April 14
British Society for Rheumatology guideline on management of adult and juvenile onset Sjögren disease.Rheumatology 2024 April 17
Albumin: a comprehensive review and practical guideline for clinical use.European Journal of Clinical Pharmacology 2024 April 13
Renin-Angiotensin-Aldosterone System: From History to Practice of a Secular Topic.International Journal of Molecular Sciences 2024 April 5
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app
All material on this website is protected by copyright, Copyright © 1994-2024 by WebMD LLC.
This website also contains material copyrighted by 3rd parties.
By using this service, you agree to our terms of use and privacy policy.
Your Privacy Choices
You can now claim free CME credits for this literature searchClaim now
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app