Effect of Different Irrigants Applied After Post Space Preparation on Push-Out Bond Strength of a Self-Etch Resin Cement.
Objectives: The aim was to investigate the effect of intracanal irrigants and agents on the bond strength of intraradicular fiber posts to dentin.
Materials and Methods: Root canals of 72 decoronated single-rooted premolars were cleaned, shaped, and obturated with gutta-percha and AH26. The specimens were incubated at 37°C and 100% humidity for seven days. Next, the coronal 10 mm of the canals were prepared to receive size 2 D.T. Light fiber post, and the specimens were randomly allocated into six groups according to the irrigants used after post space preparation: normal saline (control group), 5.25% sodium hypochlorite (NaOCl)/15 seconds, 17% ethylenediaminetetraacetic acid (EDTA)/60 seconds, 2% chlorhexidine (CHX)/5 minutes, MTAD/5 minutes, and acid-etching/15 seconds. All canals were rinsed with normal saline and dried. Fiber posts were cemented using Panavia F2.0. After 24 hours, two mid-root slices of 1mm thickness were obtained from each specimen. Push-out bond strength test was performed in a universal testing machine at 0.5mm/minute. The maximum applied load was recorded, and the bond strength was calculated in megapascal (MPa). Data were analyzed by one-way analysis of variance (ANOVA) and Tukey's test.
Results: The mean shear bond strengths of etched (53.21±12.11 MPa), MTAD (52.47±14.75 MPa) and EDTA (49.08±10.19 MPa) groups were significantly higher than that of the control group (39.82±10.04 MPa). The difference was marginally significant for CHX group (49.8±13.57 MPa) and not significant for NaOCl group (47.15±17.64 MPa).
Conclusions: Etching or irrigating the root canals with MTAD or EDTA after post space preparation increases the bond strength of Panavia F2.0 to dentin.
Materials and Methods: Root canals of 72 decoronated single-rooted premolars were cleaned, shaped, and obturated with gutta-percha and AH26. The specimens were incubated at 37°C and 100% humidity for seven days. Next, the coronal 10 mm of the canals were prepared to receive size 2 D.T. Light fiber post, and the specimens were randomly allocated into six groups according to the irrigants used after post space preparation: normal saline (control group), 5.25% sodium hypochlorite (NaOCl)/15 seconds, 17% ethylenediaminetetraacetic acid (EDTA)/60 seconds, 2% chlorhexidine (CHX)/5 minutes, MTAD/5 minutes, and acid-etching/15 seconds. All canals were rinsed with normal saline and dried. Fiber posts were cemented using Panavia F2.0. After 24 hours, two mid-root slices of 1mm thickness were obtained from each specimen. Push-out bond strength test was performed in a universal testing machine at 0.5mm/minute. The maximum applied load was recorded, and the bond strength was calculated in megapascal (MPa). Data were analyzed by one-way analysis of variance (ANOVA) and Tukey's test.
Results: The mean shear bond strengths of etched (53.21±12.11 MPa), MTAD (52.47±14.75 MPa) and EDTA (49.08±10.19 MPa) groups were significantly higher than that of the control group (39.82±10.04 MPa). The difference was marginally significant for CHX group (49.8±13.57 MPa) and not significant for NaOCl group (47.15±17.64 MPa).
Conclusions: Etching or irrigating the root canals with MTAD or EDTA after post space preparation increases the bond strength of Panavia F2.0 to dentin.
Full text links
Related Resources
Trending Papers
Autoimmune Hemolytic Anemias: Classifications, Pathophysiology, Diagnoses and Management.International Journal of Molecular Sciences 2024 April 13
Executive Summary: State-of-the-Art Review: Unintended Consequences: Risk of Opportunistic Infections Associated with Long-term Glucocorticoid Therapies in Adults.Clinical Infectious Diseases 2024 April 11
Clinical practice guidelines on the management of status epilepticus in adults: A systematic review.Epilepsia 2024 April 13
Finerenone: From the Mechanism of Action to Clinical Use in Kidney Disease.Pharmaceuticals 2024 March 27
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app
All material on this website is protected by copyright, Copyright © 1994-2024 by WebMD LLC.
This website also contains material copyrighted by 3rd parties.
By using this service, you agree to our terms of use and privacy policy.
Your Privacy Choices
You can now claim free CME credits for this literature searchClaim now
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app