[Evaluation of the effect of modified wet particle erosion on bond strength between 3Y-TZP zirconia framework and veneering porcelain].
Shanghai Kou Qiang Yi Xue = Shanghai Journal of Stomatology 2017 Februrary
PURPOSE: To evaluate the effect of bond strength between 3mol% yttrium-stabilized tetragonal zirconium polycrystal (3Y-TZP) zirconia framework after modified wet particle erosion and veneering porcelain.
METHODS: A total of 174 [8 mm× 8 mm× 3 mm (±0.02)] specimens were prepared and then randomly divided into different groups according to different particle size, sandblasting pressure, sandblasting time through conventional sandblasting (experimental groups); specimens in the control group were not sandblasted. The bond strength between 3Y-TZP zirconia framework and veneering porcelain was measured using a universal testing machine. Statistical analysis was performed using SPSS17.0 software package. The bond strength of specimens treated by two methods-conventional sandblasting and modified wet particle erosion under the same condition (150 μm, 0.6 MPa, 30 s) were acquired, while the surface was analyzed microscopically before the specimens were veneered with the veneering ceramic under scanning electronic microscope (SEM).
RESULTS: The bond strength of conventional sandblasting group under the condition (110 μm, 0.4 MPa,30 s) was maximal, and significantly higher than the control group (P<0.05). The bond strength of modified wet particle erosion group was significantly higher than the conventional sandblasting group and control group (P<0.01); SEM showed that the surface of specimen with modified wet particle erosion was homogeneously rough; the surface specimen with conventional sandblasting was heterogeneously rough, some microcracks were seen in some areas.
CONCLUSIONS: Sandblasting can slightly enhance the bond strength between 3Y-TZP zirconia framework and veneering porcelain, modified wet particle erosion is recommended for 3Y-TZP zirconia framework surface treatment.
METHODS: A total of 174 [8 mm× 8 mm× 3 mm (±0.02)] specimens were prepared and then randomly divided into different groups according to different particle size, sandblasting pressure, sandblasting time through conventional sandblasting (experimental groups); specimens in the control group were not sandblasted. The bond strength between 3Y-TZP zirconia framework and veneering porcelain was measured using a universal testing machine. Statistical analysis was performed using SPSS17.0 software package. The bond strength of specimens treated by two methods-conventional sandblasting and modified wet particle erosion under the same condition (150 μm, 0.6 MPa, 30 s) were acquired, while the surface was analyzed microscopically before the specimens were veneered with the veneering ceramic under scanning electronic microscope (SEM).
RESULTS: The bond strength of conventional sandblasting group under the condition (110 μm, 0.4 MPa,30 s) was maximal, and significantly higher than the control group (P<0.05). The bond strength of modified wet particle erosion group was significantly higher than the conventional sandblasting group and control group (P<0.01); SEM showed that the surface of specimen with modified wet particle erosion was homogeneously rough; the surface specimen with conventional sandblasting was heterogeneously rough, some microcracks were seen in some areas.
CONCLUSIONS: Sandblasting can slightly enhance the bond strength between 3Y-TZP zirconia framework and veneering porcelain, modified wet particle erosion is recommended for 3Y-TZP zirconia framework surface treatment.
Full text links
Related Resources
Trending Papers
Autoimmune Hemolytic Anemias: Classifications, Pathophysiology, Diagnoses and Management.International Journal of Molecular Sciences 2024 April 13
Executive Summary: State-of-the-Art Review: Unintended Consequences: Risk of Opportunistic Infections Associated with Long-term Glucocorticoid Therapies in Adults.Clinical Infectious Diseases 2024 April 11
Clinical practice guidelines on the management of status epilepticus in adults: A systematic review.Epilepsia 2024 April 13
Finerenone: From the Mechanism of Action to Clinical Use in Kidney Disease.Pharmaceuticals 2024 March 27
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app
All material on this website is protected by copyright, Copyright © 1994-2024 by WebMD LLC.
This website also contains material copyrighted by 3rd parties.
By using this service, you agree to our terms of use and privacy policy.
Your Privacy Choices
You can now claim free CME credits for this literature searchClaim now
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app