Effect of Temperature on the Cyclic Fatigue Resistance and Phase Transformation Behavior of Three Different NiTi Endodontic Instruments.

Background This study aims to analyze the phase transformation behavior and evaluate the effect of different temperatures on the fracture strength of files. Methodology A total of 108 files were used, and cyclic fatigue tests were performed on HyFlex EDM, VDW.ROTATE, and TruNatomy at three different temperatures (+4°C, +35°C, and +60°C) The time to fracture of files was measured, and the number of cycles was calculated. In addition, the fractured fragment lengths were measured. The Kruskal-Wallis test was used to compare the data that were not normally distributed according to groups. The Mann-Whitney U test was performed for comparisons. P-values <0.05 were considered statistically significant. Results As the temperature increased for all files, the number of cycles to fracture (NCF) decreased. NCF was significantly higher for ROTATE at 4°C and 60°C and HyFlex EDM at 35°C. Conclusions The resistance to cyclic fatigue in all files decreased significantly as the temperature increased.