Performance evaluation of dextran-coated CaFe 12 O 19 /MnFe 2 O 4 exchange-spring composites for the self-heating properties at radio frequency field.

The CaFe12 O19 /MnFe2 O4 composites with the hard (CaFe12 O19 ) and soft (MnFe2 O4 ) magnetic phases, were prepared by chemical co-precipitation method. The prepared composites were calcined at three different temperatures to form different phases. The structural, morphological, and magnetic properties of composite were analyzed by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), room temperature vibrational sample magnetometer (VSM), and transmission electron microscopy (TEM). The presence of the hard and soft phases has been confirmed without any secondary phase from XRD analysis, indicating the formation of composite. The crystallite size is found to be in the range of 24-44 nm calculated by Scherrer's formula. The TEM revealed hexagonal platelets of CaFe12 O19 with spinel MnFe2 O4 particles with an average particle size of 48 nm formed at the surface of the CaFe12 O19 /MnFe2 O4 composite. The room temperature magnetic properties of composite were evaluated by employing VSM. The magnetic measurements have displayed enhancement in coercivity and magnetization for CaFe12 O19 /MnFe2 O4 , indicating that the composite possessed excellent exchange coupling. The composite's enhanced energy product ((BH)max ) made it highly promising for biomedical applications such as hyperthermia. The exchange-spring coupled magnetic composite was coated with dextran to make it biocompatible, which is necessary for hyperthermia applications. The coating was confirmed using Fourier transform infrared spectroscopy (FTIR). Cytotoxicity tests on Vero cell lines showed that the coated composites had an excellent (>95%) cell survival rate. The hyperthermia heating of composite was measured for different concentrations of composite (0.25, 0.5, 1, 2, and 4 mg/mL) from which specific loss power (SLP) was calculated. From these SLP values, the optimized concentration was identified.