Analysis of the cytotoxicity and bioactivity of CeraSeal, BioRoot™ and AH Plus ® sealers in pre-osteoblast lineage cells.

BACKGROUND: The objective of the present study was to evaluate in vitro the cytotoxicity and bioactivity of various endodontic sealers (CeraSeal, BioRoot™ and AH Plus® ) in pre-osteoblast mouse cells (MC3T3 cells).

METHODS: MC3T3 cells (ATCC CRL-2594) were plated in 1 × 104 cells/well in 96-well plates in contact with endodontic sealers at concentrations of 1:10 and 1:100. Cell viability was evaluated by MTT assay after 24 and 48 h. In addition, sealer bioactivity was measured by RT-PCR for mediator of inflammation (Tnf, Ptgs2) and mineralization (Runx2, Msx1, Ssp1 and Dmp1) after 24 h and by Alizarin Red S Assay of mineralization after 28 days. Data were analyzed using one-way ANOVA followed by the Tukey's post-test at a significance level of 5%.

RESULTS: BioRoot™ presented 24-hour cytotoxicity (p < 0.05) at 1:10 concentration. In the period of 48 h, no endodontic cement was cytotoxic to the cells compared to the control (p > 0.05). TNF-α gene expression was induced by AH Plus® (p < 0.05), while Ptgs2 was induced by the CeraSeal and BioRoot™ (p < 0.05). The expression of Runx2 was stimulated by BioRoot™ and AH Plus® (p < 0.05). In contrast, the expression of Dmp-1 Dmp1 was higher for the CeraSeal and BioRoot™ (p < 0.05). Nonetheless, the sealers did not impact the formation of mineralization nodules (p > 0.05).

CONCLUSION: CeraSeal, BioRoot™ and AH Plus® sealers were not cytotoxic to MC3T3 cells within 48 h, but differentially induced the expression of genes related to inflammation and mineralization without impacting biomineralization by the cells.