Effect of Load Cycling on the Fracture Strength/Mode of Teeth Restored with FRC Posts or a FRC Liner and a Resin Composite.

The aim of the study was to comparatively evaluate the fracture strength and mode of root canal treated teeth restored with resin composites with and without posts. The lingual cusps of root canal treated first upper premolars (n = 10/group) were removed down to cervical enamel and restored with the following: group A: glass-fiber post (Glassix) followed by a particulate-filled composite resin (PFC, G-aenial posterior, 3 × 2 mm layers); group B: glass-fiber reinforced composite bulk fill liner (EverX posterior, 4 mm layer) with the PFC (2 mm layer). Specimens were immersed in H2 O (1 w/37°C), then subjected to load cycling (50 N/0.2 Hz/200k cycles), and fractured under compressive loading. Failure mode was characterized by stereomicroscopy. Statistical analysis was performed by Mann-Whitney (load) and Chi-square (mode) at a = 0.05. No statistically significant differences (p = 0.273) were found in fracture load between median values of groups A (860 N) and B (1059 N). In group A, 60% of the specimens demonstrated catastrophic root fractures and 40% mixed crown fractures (tooth cusp and restoration), whereas in group B, no root fractures were found, and the failure modes were equally distributed between mixed fractures as above and fracture of the buccal cusp. These differences were statistically significant (p = 0.004). The combination of the glass-FRC bulk fill liner with the PFC diminished the catastrophic root fractures induced by FRC posts, at a similar or higher fracture load.