Deflection Evaluation of Thermoactivated Nickel-Titanium Archwires after Heat Treatment on their Distal Ends.

OBJECTIVE: This study evaluated in vitro the mechanical changes of 0.018" (0.45 mm) and 0.016 × 0.022" (0.40 × 0.55 mm) thermoactivated nickel-titanium archwires subjected to heat treatment on their distal ends.

MATERIALS AND METHODS: Ten archwires in diameters 0.018" and 0.016 × 0.022" by different manufacturers Ormco, Morelli, Orthometric and Unitek were tested. Each tested archwire had an experimental side, submitted to heat treatment, and an annealing-free control. Tests for load/deflection were performed using a universal testing machine, with temperature control in the austenitic transformation phase through tempe rature-controlled chamber. The variables showed normal distribution (Kolmogorov-Smirnov), the t-student test was applied in order to observe the difference between the experi mental and control groups. Statistical significance was set at p < 0.05.

RESULTS: There were no statistically significant differences between the groups.

CONCLUSION: Heat treatment carried out in the region corresponding to the first molar distal region on thermoactivated nickel-titanium archwires did not influence the load/deflection values in adjacent portion.