Effect of Particle Size and Application Pressure in Air-Borne Particle Abrasion on the Adhesion of Polyetheretherketone.
European Journal of Prosthodontics and Restorative Dentistry 2024 Februrary 22
INTRODUCTION: This study aims to investigate the effect of different particle sizes and pressures on the shear bond strength (SBS) and the roughness (Ra) of polyetheretherketone.
MATERIALS AND METHODS: A total of 117 polyetheretherketone specimens were fabricated and divided into a control (CN: no air-particle abrasion) and eight pre-treatment groups (air-abraded with 50- or 110-μm Al2O3 particles at 1(A), 1.5(B), 2(C), and 2.5(D) bar). The adhesive, Visio.link was used. Thermal aging was performed. Surface properties, SBS and failure mode were assessed. Data was analyzed by linear regression, Pearson correlation and Dunnett's T3 test for pairwise comparisons (p⟨0.05).
RESULTS: The highest and lowest Ra were found in the 110D and CN groups respectively, and the highest SBS results were obtained from the 50B group. Pressure and particle size showed significant difference on the investigated properties (p⟨0.001). Only adhesive failure was observed in the CN, and resin cohesive failure was observed in addition to adhesive failure in the overall study groups.
CONCLUSION: The air-borne particle abrasion procedures and the adhesive material combination are critical to the strength of the polyetheretherketone bond. The combination of visio.link with the pre-treatment option of 50-μm Al₂O₃ particles applied at 1.5-bar pressure delivered the most favorable results.
MATERIALS AND METHODS: A total of 117 polyetheretherketone specimens were fabricated and divided into a control (CN: no air-particle abrasion) and eight pre-treatment groups (air-abraded with 50- or 110-μm Al2O3 particles at 1(A), 1.5(B), 2(C), and 2.5(D) bar). The adhesive, Visio.link was used. Thermal aging was performed. Surface properties, SBS and failure mode were assessed. Data was analyzed by linear regression, Pearson correlation and Dunnett's T3 test for pairwise comparisons (p⟨0.05).
RESULTS: The highest and lowest Ra were found in the 110D and CN groups respectively, and the highest SBS results were obtained from the 50B group. Pressure and particle size showed significant difference on the investigated properties (p⟨0.001). Only adhesive failure was observed in the CN, and resin cohesive failure was observed in addition to adhesive failure in the overall study groups.
CONCLUSION: The air-borne particle abrasion procedures and the adhesive material combination are critical to the strength of the polyetheretherketone bond. The combination of visio.link with the pre-treatment option of 50-μm Al₂O₃ particles applied at 1.5-bar pressure delivered the most favorable results.
Full text links
Related Resources
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app
All material on this website is protected by copyright, Copyright © 1994-2024 by WebMD LLC.
This website also contains material copyrighted by 3rd parties.
By using this service, you agree to our terms of use and privacy policy.
Your Privacy Choices
You can now claim free CME credits for this literature searchClaim now
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app