Effect of Post-Space Irrigation with NaOCl And CaOCl at Different Concentrations on the Bond Strength of Posts Cemented with a Self-Adhesive Resin Cement.

The aim of this study was to evaluate the effect of post-space irrigation with NaOCl and CaOCl at different concentrations on the bond strength of posts cemented with a self-adhesive resin cement. Eighty premolars were sectioned 14 mm from the apex, and endodontically treated. The root canal filling was partially removed. Specimens were randomly assigned into 8 groups (n=10), according to the irrigant for post-space irrigation: SS - 0.9% saline solution (control group); CHX - 2% chlorhexidine; 1% NaOCl - 1% sodium hypochlorite; 2.5% NaOCl - 2.5% sodium hypochlorite; 5% NaOCl - 5% sodium hypochlorite; 1% CaOCl - 1% calcium hypochlorite; 2.5% CaOCl - 2.5% calcium hypochlorite; and 5% CaOCl - 5% calcium hypochlorite. For each group, irrigation was performed continuously with 2 ml of solution. The post-spaces were dried with paper points (#80), and glass fiber posts were cemented using a self-adhesive resin cement. The specimens were sectioned perpendicularly and the push-out test was performed. Optical microscopy was used to analyze the failure mode. ANOVA and Bonferroni tests analyzed the bond strength data. NaOCl and CaOCl presented similar bond strength regardless the concentration used to irrigate the post-space (p>0.05). SS showed the highest bond strength (11.47 MPa) (p<0.05). Adhesive failures at the cement/dentin interface were predominant (58.33%). Saline solution should be irrigant of choice to irrigate the post-space before fiber post cementation with self-adhesive resin cement. NaOCl and CaOCl negatively affect the bond strength values.