Effect of airborne-particle abrasion and, acid and alkaline treatments on shear bond strength of dental zirconia.
Dental Materials Journal 2019 March 32
The surface roughness, morphology and shear bond strength (SBS) of dental zirconia using three different surface treatment techniques were evaluated. Three groups of sintered zirconia blocks were treated as follow, 1) Airborne-particle abrasion (APA) group (G1-APA), 50-µm Al2 O3 ; 2) APA and 9% hydrofluoric acid etching (G2-HF); 3) APA and Sodium Hydroxide (G3-NaOH). The specimens were evaluated for roughness [atomic force microscope (AFM)], morphology [Scanning Electron Microscope (SEM)] and for SBS in the universal testing machine. The AFM revealed changes in the roughness after the surface treatments, however there was not Ra difference between groups, SEM analysis revealed changes in surface morphology for all surface treated specimens. For SBS, significant difference was found between G1-APA=8.4±2.7 MPa and G2-HF=3.3±0.6 MPa (p<0.05) and G2-HF and G3-NaOH=9.0±3.0 MPa (p<0.05). The main fracture mode was mixed failure (63%) for G1-APA and G3-NaOH groups. G2-HF showed 100% adhesive failure. SBS was improved with NaOH, however application of HF significantly decreased SBS.
Full text links
Related Resources
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app
All material on this website is protected by copyright, Copyright © 1994-2024 by WebMD LLC.
This website also contains material copyrighted by 3rd parties.
By using this service, you agree to our terms of use and privacy policy.
Your Privacy Choices
You can now claim free CME credits for this literature searchClaim now
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app