Evaluation of Adhesion Between Carbon Fiber Frameworks and Esthetic Veneering Materials.
International Journal of Prosthodontics 2018 September
PURPOSE: To assess bond strength and failure patterns of carbon fiber-reinforced composite (CFRC) and veneering materials.
MATERIALS AND METHODS: A total of 20 samples were prepared: 10 veneered with polymethylmethacrylate (group A) and 10 with composite resin (group B). Shear bond strength (SBS) was measured, and failed samples were microscopically observed.
RESULTS: The mean ± standard deviation (SD) SBS of specimens in group A was slightly higher (7.39 ± 0.24 MPa) than specimens in group B (5.68 ± 0.29 MPa). Microscopic observation showed an adhesive fracture pattern at the CFRC-adhesive interface in both groups.
CONCLUSION: Adhesion between CFRC and veneering material is reliable and predictable, although a specific protocol needs to be developed to improve adhesion.
MATERIALS AND METHODS: A total of 20 samples were prepared: 10 veneered with polymethylmethacrylate (group A) and 10 with composite resin (group B). Shear bond strength (SBS) was measured, and failed samples were microscopically observed.
RESULTS: The mean ± standard deviation (SD) SBS of specimens in group A was slightly higher (7.39 ± 0.24 MPa) than specimens in group B (5.68 ± 0.29 MPa). Microscopic observation showed an adhesive fracture pattern at the CFRC-adhesive interface in both groups.
CONCLUSION: Adhesion between CFRC and veneering material is reliable and predictable, although a specific protocol needs to be developed to improve adhesion.
Full text links
Related Resources
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app
All material on this website is protected by copyright, Copyright © 1994-2024 by WebMD LLC.
This website also contains material copyrighted by 3rd parties.
By using this service, you agree to our terms of use and privacy policy.
Your Privacy Choices
You can now claim free CME credits for this literature searchClaim now
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app