Influence of crown design and material on chipping-resistance of all-ceramic molar crowns: An in vitro study.
Dental and Medical Problems 2018 January
BACKGROUND: All-ceramic restorations have become popular and the trend is ongoing. However, the incidence of chipping within the veneering layer has been a commonly reported failure in clinical practice.
OBJECTIVES: The aim of this in vitro study was to evaluate the effect of ceramic crown design (monolithic vs bi-layered) and material on the chipping resistance of molar crowns submitted to compressive cyclic loading.
MATERIAL AND METHODS: Fifty identical epoxy resin replicas of a mandibular first molar with crown preparation were divided into 5 groups (n = 10) as follows: the MLD group - monolithic CAD/CAM lithium-disilicate glass-ceramic (LDGC) crowns; 30 zirconia cores were veneered with either feldspathic porcelain by hand-layering technique (ZHL) or by heat-pressing technique (ZVP), or with milled LDGC veneers and subsequently fused to the cores (ZLD); 10 porcelain-fused-to-metal (PFM) crowns acted as a control group. All crowns were cemented using Panavia® F2.0 resin cement (Kuraray Dental, Tokyo, Japan). After storage in water at 37°C for 1 week, the specimens were subjected to compressive cyclic loading at the mesiobuccal cusp which was tilted at 30°. A load cycle of 50-450 N was used and specimens were maintained in an aqueous environment throughout 500,000 cycles in a universal testing machine (Instron, Norwood, USA). The data was statistically analyzed at 5% significant level with Fisher's exact test and Kaplan-Meier survival analysis.
RESULTS: Significant differences in survival rates of the specimens used in the groups (p < 0.001) were found. Specimens of the PFM, ZHL and ZVP groups underwent failures at different stages of the 500,000 fatigue cycles, while specimens of the MLD and ZLD groups survived the entire fatigue test. ZHL and ZVP crowns had the worst chipping-resistance, while PFM crowns performed slightly better. The Kaplan-Meier test revealed significantly higher survival rates for the MLD and ZLD specimens compared to the other 3 groups.
CONCLUSIONS: The use of LDGC as a monolithic molar crown and as a veneer over a zirconia core resulted in superior resistance to cuspal chipping.
OBJECTIVES: The aim of this in vitro study was to evaluate the effect of ceramic crown design (monolithic vs bi-layered) and material on the chipping resistance of molar crowns submitted to compressive cyclic loading.
MATERIAL AND METHODS: Fifty identical epoxy resin replicas of a mandibular first molar with crown preparation were divided into 5 groups (n = 10) as follows: the MLD group - monolithic CAD/CAM lithium-disilicate glass-ceramic (LDGC) crowns; 30 zirconia cores were veneered with either feldspathic porcelain by hand-layering technique (ZHL) or by heat-pressing technique (ZVP), or with milled LDGC veneers and subsequently fused to the cores (ZLD); 10 porcelain-fused-to-metal (PFM) crowns acted as a control group. All crowns were cemented using Panavia® F2.0 resin cement (Kuraray Dental, Tokyo, Japan). After storage in water at 37°C for 1 week, the specimens were subjected to compressive cyclic loading at the mesiobuccal cusp which was tilted at 30°. A load cycle of 50-450 N was used and specimens were maintained in an aqueous environment throughout 500,000 cycles in a universal testing machine (Instron, Norwood, USA). The data was statistically analyzed at 5% significant level with Fisher's exact test and Kaplan-Meier survival analysis.
RESULTS: Significant differences in survival rates of the specimens used in the groups (p < 0.001) were found. Specimens of the PFM, ZHL and ZVP groups underwent failures at different stages of the 500,000 fatigue cycles, while specimens of the MLD and ZLD groups survived the entire fatigue test. ZHL and ZVP crowns had the worst chipping-resistance, while PFM crowns performed slightly better. The Kaplan-Meier test revealed significantly higher survival rates for the MLD and ZLD specimens compared to the other 3 groups.
CONCLUSIONS: The use of LDGC as a monolithic molar crown and as a veneer over a zirconia core resulted in superior resistance to cuspal chipping.
Full text links
Related Resources
Trending Papers
Challenges in Septic Shock: From New Hemodynamics to Blood Purification Therapies.Journal of Personalized Medicine 2024 Februrary 4
Molecular Targets of Novel Therapeutics for Diabetic Kidney Disease: A New Era of Nephroprotection.International Journal of Molecular Sciences 2024 April 4
The 'Ten Commandments' for the 2023 European Society of Cardiology guidelines for the management of endocarditis.European Heart Journal 2024 April 18
A Guide to the Use of Vasopressors and Inotropes for Patients in Shock.Journal of Intensive Care Medicine 2024 April 14
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app
All material on this website is protected by copyright, Copyright © 1994-2024 by WebMD LLC.
This website also contains material copyrighted by 3rd parties.
By using this service, you agree to our terms of use and privacy policy.
Your Privacy Choices
You can now claim free CME credits for this literature searchClaim now
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app