Oxidation Behavior of Tyranno ZMI-SiC Fiber/SiC-SiBC Matrix Composite from 800 to 1200 °C.

In this work, the self-healing Si-B-C matrix-modified ZMI-SiC fiber/SiC (SiC/SiC-SiBC) composite was prepared by a combined process of chemical vapor infiltration, slurry infiltration, and liquid silicon infiltration. The weight changes of the as-fabricate composite after oxidation at 800, 1000, and 1200 °C for 100 h were -0.41%, -0.06%, +0.05%, respectively. The corresponding strength retention ratios were 75%, 99%, 100%, respectively. With the increase of oxidation temperature, coating cracks would be closed. A dense oxidation film was formed with the oxidation of the SiBC matrix, preventing the oxidation of interphase and fiber and leading to excellent oxidation resistance at 1000 and 1200 °C.