Application of Calcium Silicate Materials After Acid Etching May Preserve Resin-Dentin Bonds.
Operative Dentistry 2018 September
INTRODUCTION: The aim of the present study was to evaluate the effect of the application of calcium silicate materials (CSMs), after acid etching, on the longevity of the hybrid layer and marginal adaptation of composite restorations.
METHODS AND MATERIALS: Eighty human permanent molars received an intrapulpal pressure of 15 cm H2 O. Sixty teeth received a mesial proximal slot preparation with the gingival margin extending 1 mm below the cemento-enamel junction. The samples were divided into two groups. Group 1 received restorations using two types of etch-and-rinse adhesives: ethanol based (Single Bond, 3M ESPE, St Paul, MN, USA) and acetone based (Prime & Bond NT, Dentsply, DeTrey GmbH, Germany). In group 2 samples, a commercially available CSM (ProRoot MTA) was allowed to set before grinding and placing into a distilled water solution. This solution was applied on the cavity floor after acid etching. The surface was washed after 30 seconds followed by application of adhesives and restorations as in group 1. The samples were stored in phosphate-buffered saline for six months, maintaining the intrapulpal pressure. An epoxy replica was made, and the marginal adaptation was evaluated using scanning electron microscopy. The percentage of continuous margin (CM) was recorded for each group. Another 20 samples were used for hybrid layer evaluation. The crowns were ground to expose dentin. Intrapulpal pressure was applied. The samples were divided into two groups and restored similar to samples restored for marginal adaptation evaluation. The samples were longitudinally cut in 1-mm slices. The slices were stored under 15 cm of phosphate-buffered saline to simulate the pulpal pressure. After six months, the adhesive interface was evaluated using a scanning electron microscope. Statistical analysis was done with two-way analysis of variance with Holm-Sidak's correction for multiple comparisons.
RESULTS: Application of CSMs improved the marginal adaptation values in both adhesive groups. In group 1, there were areas of incomplete penetration of resins along with evidence of partial degradation of resin tags. Samples receiving CSM application after acid etching demonstrated long and regular resin tags with very few signs of degradation.
CONCLUSIONS: Application of CSMs after acid etching can be a potential avenue in preserving the resin-dentin bonds.
METHODS AND MATERIALS: Eighty human permanent molars received an intrapulpal pressure of 15 cm H2 O. Sixty teeth received a mesial proximal slot preparation with the gingival margin extending 1 mm below the cemento-enamel junction. The samples were divided into two groups. Group 1 received restorations using two types of etch-and-rinse adhesives: ethanol based (Single Bond, 3M ESPE, St Paul, MN, USA) and acetone based (Prime & Bond NT, Dentsply, DeTrey GmbH, Germany). In group 2 samples, a commercially available CSM (ProRoot MTA) was allowed to set before grinding and placing into a distilled water solution. This solution was applied on the cavity floor after acid etching. The surface was washed after 30 seconds followed by application of adhesives and restorations as in group 1. The samples were stored in phosphate-buffered saline for six months, maintaining the intrapulpal pressure. An epoxy replica was made, and the marginal adaptation was evaluated using scanning electron microscopy. The percentage of continuous margin (CM) was recorded for each group. Another 20 samples were used for hybrid layer evaluation. The crowns were ground to expose dentin. Intrapulpal pressure was applied. The samples were divided into two groups and restored similar to samples restored for marginal adaptation evaluation. The samples were longitudinally cut in 1-mm slices. The slices were stored under 15 cm of phosphate-buffered saline to simulate the pulpal pressure. After six months, the adhesive interface was evaluated using a scanning electron microscope. Statistical analysis was done with two-way analysis of variance with Holm-Sidak's correction for multiple comparisons.
RESULTS: Application of CSMs improved the marginal adaptation values in both adhesive groups. In group 1, there were areas of incomplete penetration of resins along with evidence of partial degradation of resin tags. Samples receiving CSM application after acid etching demonstrated long and regular resin tags with very few signs of degradation.
CONCLUSIONS: Application of CSMs after acid etching can be a potential avenue in preserving the resin-dentin bonds.
Full text links
Related Resources
Trending Papers
Challenges in Septic Shock: From New Hemodynamics to Blood Purification Therapies.Journal of Personalized Medicine 2024 Februrary 4
Molecular Targets of Novel Therapeutics for Diabetic Kidney Disease: A New Era of Nephroprotection.International Journal of Molecular Sciences 2024 April 4
The 'Ten Commandments' for the 2023 European Society of Cardiology guidelines for the management of endocarditis.European Heart Journal 2024 April 18
A Guide to the Use of Vasopressors and Inotropes for Patients in Shock.Journal of Intensive Care Medicine 2024 April 14
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app
All material on this website is protected by copyright, Copyright © 1994-2024 by WebMD LLC.
This website also contains material copyrighted by 3rd parties.
By using this service, you agree to our terms of use and privacy policy.
Your Privacy Choices
You can now claim free CME credits for this literature searchClaim now
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app