Membrane bioreactors troubleshooting through the preparation of a high antifouling PVDF ultrafiltration mixed-matrix membrane blended with O-carboxymethyl chitosan-Fe 3 O 4 nanoparticles.

Polymeric ultrafiltration (UF) membranes often used in membrane bioreactor (MBR) prone to be fouled by fouling agents. Therefore, in this paper, the antifouling characteristics of polyvinylidene fluoride (PVDF) UF membranes for wastewater treatment are improved through modifying membranes by O-carboxymethyl chitosan (OCMCS)-functionalized Fe3 O4 nanoparticles (OCMCSFe3 O4 ). The modifier agent was manufactured by the adsorption of OCMCS on Fe3 O4 nanoparticles, which were synthesized via co-precipitating method. Antifouling performance of membranes was assessed by permeation tests done using activated sludge suspension as a biological foulant, then the calculation of the pure water flux recovery ratio (FRR) and fouling resistance parameters. Also, to investigate the protein rejection of membranes, permeation tests were conducted by the bovine serum albumin (BSA) solution. According to the obtained results, surface hydrophilicity of the embedded membranes was improved in the low concentrations of the modified nanoparticles. However, the high quantity of the OCMCS-Fe3 O4 nanoparticles (>0.1 wt. %) in the casting solution lessened membrane performance owing to the agglomeration of the nanoparticles in the polymer matrix. Although, the 1 wt. % OCMCS-Fe3 O4 membrane revealed considerably higher PWF and permeation than that of the other membranes. It was because of defects and cracks in the membranes. The 0.05 wt. % OCMCS-Fe3 O4 /PVDF membrane exhibited the highest FRR (95.7%) and protein rejection value (48%) and the lowest irreversible fouling resistance (Rir) value (4.2%). It is concluded that the blended membranes with modified nanoparticles resulted in a high-flux ultrafiltration membrane comparable with microfiltration membrane, while its separation properties remained similar to UF membrane.