Flexural Strength of Glass Carbomer Cement and Conventional Glass Ionomer Cement Stored in Different Storage Media over Time.

OBJECTIVES: Glass ionomer cement (GIC) is routinely placed as a restorative material in dentistry. However, due to its poor physical properties, its use is limited to cases where the level of stress on restoration is minimal. Improved formulations of GIC have been developed to overcome these drawbacks. The purpose of this study was to evaluate flexural strength of a conventional GIC (Fuji IX) against a newly developed glass carbomer cement (GCP).

MATERIALS AND METHODS: For Fuji IX and GCP, a total of 80 blocks were prepared and divided into 16 groups (n = 5). These groups were further categorized according to the storage medium (artificial saliva and Vaseline) and time intervals (24 h and 1, 2, and 4 weeks). A 3-point bending test was carried out, and statistical analysis was done using ANOVA and Tukey post hoc tests.

RESULTS: Fuji IX showed a mean flexural strength of 25.14 ± 13.02 versus 24.27 ± 12.57 MPa for GCP. There was no significant statistical difference between both materials when compared under storage media. Both materials showed the highest value for flexural strength at 2 weeks of storage and lowest at 4 weeks.

CONCLUSION: The storage media do not affect the flexural strength of the specimens with reference to time. Time is the unique factor with relative influence on mean resistance to fracture. Further testing is required to evaluate the true potential of the newly developed GCP.