Comparative evaluation of the amount of the residual monomer in conventional and deep-frozen heat cure polymethylmethacrylate acrylic resin: An in vitro study.

Statement of Problem: Heat cure acrylic resin material with reduced monomer content is generally recommended for clinical usage as it leads to improved mechanical, physical, and biocompatibility properties.

Aims and Objective: The purpose of the present study was to evaluate and compare the amount of the residual monomer in the conventional and three different groups of deep-frozen heat cure polymethylmethacrylate (PMMA) acrylic resin.

Materials and Methods: Totally 40 Specimens of heat cure PMMA acrylic resin (DPI India) (10 conventional heat cure and 30 deep frozen) were made using two disc-shaped stainless steel molds and invested into type II dental stone using compression molding technique. Each group contained 10 specimens ( n = 10). Group 1: Control group of conventional polished PMMA specimen stored in water for 24 h at +37°C (10 specimens), Group 2: Deep frozen unpolished PMMA (10 specimens), Group 3: Deep frozen polished PMMA (10 specimens), and Group 4: Deep frozen polished PMMA specimen stored in water for 24 h at +37°C (10 specimens). Amount of the residual monomer content in all the specimens was measured using high-performance liquid chromatography. Data were analyzed using One-Way Analysis of Variance and multiple comparison Tukey's post hoc test (α = 0.05).

Results: Least residual monomer content was found in Group 4 (0.12 wt%) followed by Group 3 (0.19 wt%), Group 2 (0.23 wt%), and Group 1 (0.26 wt%). Statistically significant difference ( P < 0.05) was found in residual monomer content for all the four groups tested. Post hoc test for intergroup comparison also showed a significant difference between groups.

Conclusion: The amount of the residual monomer was found to be least in deep-frozen polished PMMA specimen stored in water for 24 h at +37°C (Group 4). Thus, it can be concluded that deep freezing, polishing, and storing in water can reduce the residual monomer content.