Fracture load of metal-ceramic, monolithic, and bi-layered zirconia-based posterior fixed dental prostheses after thermo-mechanical cycling.
Journal of Dentistry 2018 June
OBJECTIVES: This study aims to evaluate the fracture load of differently fabricated 3-unit posterior fixed dental prostheses (FDPs) with an intermediate pontic.
METHODS: Fifty sets of two stainless-steel abutments were randomly assigned to five groups (n = 10 each) depending on the material and technique used for manufacturing the FDPs: (1) Metal-ceramic (MC, control); (2) Lava Zirconia (LZ, bi-layered); (3) Lava Plus (LM, monolithic); (4) VITA In-Ceram YZ (YZ, bi-layered); and (5) IPS e-max ZirCAD (ZZ, bi-layered). After being luted to the dies, all FDPs were submitted to thermo-mechanical cycling (120,000 masticatory cycles, 50 N; plus 774 thermal cycles of 5 °C/55 °C, dwell time: 30 s). Samples were then subjected to a three-point bending test until fracture in a universal testing machine (cross-head speed: 1 mm/min). Fracture load of the veneering ceramic (VF) and total fracture load (TF) were recorded. Microstructure and failure patterns were assessed. Data was analysed using one-way ANOVA and Tukey HSD post-hoc tests (α = 0.05).
RESULTS: MC restorations recorded higher VF and TF values than did zirconia FDPs (p = 0.0001), which showed no between-group differences. Within the bi-layered groups, TF was significantly higher than VF. LM pieces registered lower average grain size than did LZ specimens (p = 0.001). Overall, the connector was the weakest part.
CONCLUSIONS: All of the groups tested could withstand clinical chewing forces in terms of average fracture load. Zirconia-based samples performed similarly to each other, but showed lower mean fracture load values than did metal-ceramic ones.
CLINICAL SIGNIFICANCE: Monolithic zirconia may be recommendable for solving the chipping problem.
METHODS: Fifty sets of two stainless-steel abutments were randomly assigned to five groups (n = 10 each) depending on the material and technique used for manufacturing the FDPs: (1) Metal-ceramic (MC, control); (2) Lava Zirconia (LZ, bi-layered); (3) Lava Plus (LM, monolithic); (4) VITA In-Ceram YZ (YZ, bi-layered); and (5) IPS e-max ZirCAD (ZZ, bi-layered). After being luted to the dies, all FDPs were submitted to thermo-mechanical cycling (120,000 masticatory cycles, 50 N; plus 774 thermal cycles of 5 °C/55 °C, dwell time: 30 s). Samples were then subjected to a three-point bending test until fracture in a universal testing machine (cross-head speed: 1 mm/min). Fracture load of the veneering ceramic (VF) and total fracture load (TF) were recorded. Microstructure and failure patterns were assessed. Data was analysed using one-way ANOVA and Tukey HSD post-hoc tests (α = 0.05).
RESULTS: MC restorations recorded higher VF and TF values than did zirconia FDPs (p = 0.0001), which showed no between-group differences. Within the bi-layered groups, TF was significantly higher than VF. LM pieces registered lower average grain size than did LZ specimens (p = 0.001). Overall, the connector was the weakest part.
CONCLUSIONS: All of the groups tested could withstand clinical chewing forces in terms of average fracture load. Zirconia-based samples performed similarly to each other, but showed lower mean fracture load values than did metal-ceramic ones.
CLINICAL SIGNIFICANCE: Monolithic zirconia may be recommendable for solving the chipping problem.
Full text links
Related Resources
Trending Papers
Challenges in Septic Shock: From New Hemodynamics to Blood Purification Therapies.Journal of Personalized Medicine 2024 Februrary 4
Molecular Targets of Novel Therapeutics for Diabetic Kidney Disease: A New Era of Nephroprotection.International Journal of Molecular Sciences 2024 April 4
The 'Ten Commandments' for the 2023 European Society of Cardiology guidelines for the management of endocarditis.European Heart Journal 2024 April 18
A Guide to the Use of Vasopressors and Inotropes for Patients in Shock.Journal of Intensive Care Medicine 2024 April 14
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app
All material on this website is protected by copyright, Copyright © 1994-2024 by WebMD LLC.
This website also contains material copyrighted by 3rd parties.
By using this service, you agree to our terms of use and privacy policy.
Your Privacy Choices
You can now claim free CME credits for this literature searchClaim now
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app