Fabrication of hierarchical CoP nanosheet@microwire arrays via space-confined phosphidation toward high-efficiency water oxidation electrocatalysis under alkaline conditions.

Nanoscale 2018 May 4
In spite of recent advances in the synthesis of transition metal phosphide nanostructures, the simple fabrication of hierarchical arrays with more accessible active sites still remains a great challenge. In this Communication, we report a space-confined phosphidation strategy toward developing hierarchical CoP nanosheet@microwire arrays on nickel foam (CoP NS@MW/NF) using a Co(H2PO4)2·2H3PO4 microwire array as the precursor. The thermally stable nature of the anion in the precursor is key to hierarchical nanostructure formation. When used as a 3D electrode for water oxidation electrocatalysis, such CoP NS@MW/NF needs an overpotential as low as 296 mV to drive a geometrical catalytic current density of 100 mA cm-2 in 1.0 M KOH, outperforming all reported Co phosphide catalysts in alkaline media. This catalyst also shows superior long-term electrochemical durability, maintaining its activity for at least 65 h. This study offers us a general method for facile preparation of hierarchical arrays for applications.

Full text links

We have located links that may give you full text access.
Can't access the paper?
Try logging in through your university/institutional subscription. For a smoother one-click institutional access experience, please use our mobile app.

For the best experience, use the Read mobile app

Mobile app image

Get seemless 1-tap access through your institution/university

For the best experience, use the Read mobile app

All material on this website is protected by copyright, Copyright © 1994-2024 by WebMD LLC.
This website also contains material copyrighted by 3rd parties.

By using this service, you agree to our terms of use and privacy policy.

Your Privacy Choices Toggle icon

You can now claim free CME credits for this literature searchClaim now

Get seemless 1-tap access through your institution/university

For the best experience, use the Read mobile app