Hard Pd Nanorods in the Soft Surfactant Mixture of CTAB and Pluronics: Seedless Synthesis and Their Self-Assembly.

Seedless synthesis of Pd nanorods and their self-assembly into the layered smectic ordering are described. Aqueous Pluronic triblock copolymers (14.3-35.7%) are used as a soft template along with cetyltrimethylammonium bromide for inducing one-dimensional growth of Pd nanorods. Pluronic triblock copolymers are probably the most used polymer surfactants, and they are composed of poly(ethylene oxide) (PEO)-poly(propylene oxide) (PPO)-PEO triblocks. Neither pH adjustment nor AgNO3 and other additives, such as poly(vinyl pyrrolidone) and ethylene glycol, are required to obtain Pd nanorods. Sonochemical synthesis at 43 °C, followed by thermal annealing for 1 h at 65 °C produces Pd nanorods with the aspect ratio from 3.1 (17.9%, Pluronic L-64) to 6.7 (35.7%, Pluronic P-123). Two-dimensional self-assembly of the nanorods is observed, and both nematic ordering between the mesogens and smectic ordering between the layers is identified. Micellar hydrophobic PPO with hydrated PEO coronas are known to self-assemble into many crystalline orders, including cubic, hexagonal, lamellar, and inverse hexagonal mesophases, which extend into cylindrical micelles with increasing temperature. Relatively small size of Pluronic copolymers with regard to general polymers, but rather large size of their micelles and their tendency to organize into crystalline mesophases are thought to contribute to the anisotropic growth of Pd nanorods.