Effect of composite warming on shear bond strength.

Several manufacturers produce devices designed to warm composite resins used in restorative dentistry. Previous investigators have examined the effects of heating composite restorative resins prior to placement and polymerization. Heating has been reported to reduce viscosity, improve ease of placement, enhance monomer conversion, and reduce microleakage. The aim of the present study was to compare shear bond strengths of room temperature (22°C) and prewarmed (54°C) restorative composite resin. Extracted bovine mandibular incisors were sectioned sagittally and embedded in acrylic cylinders. Enamel was selectively etched with 37% phosphoric acid, rinsed, and dried. Self-etching primer was applied to both enamel and dentin. Self-etching adhesive was then applied and photopolymerized. Composite resin capsules were then divided into prewarmed and room temperature groups. Fourteen composite specimens prewarmed in an incubator were applied to the prepared enamel and dentin and photopolymerized. Fourteen room temperature composite specimens were likewise placed. After storage in water for 24 hours, all composite specimens were subjected to shear stress testing. The resulting data were analyzed with a t test (P = 0.05). There was no statistically significant difference between the shear bond strengths of the prewarmed and room temperature composite resin specimens. Warming does not appear to affect bond strength of composite resin bonded to both dentin and enamel.