Quantification of elemental area densities in multiple metal layers (Au/Ni/Cu) on a Cr-coated quartz glass substrate for certification of NMIJ CRM 5208-a.

Area densities of Au/Ni/Cu layers on a Cr-coated quartz substrate were characterized to certify a multiple-metal-layer certified reference material (NMIJ CRM5208-a) that is intended for use in the analysis of the layer area density and the thickness by an X-ray fluorescence spectrometer. The area densities of Au/Ni/Cu layers were calculated from layer mass amounts and area. The layer mass amounts were determined by using wet chemical analyses, namely inductively coupled plasma mass spectrometry (ICP-MS), isotope-dilution (ID-) ICP-MS, and inductively coupled plasma optical emission spectrometry (ICP-OES) after dissolving the layers with diluted mixture of HCl and HNO3 (1:1, v/v). Analytical results of the layer mass amounts obtained by the methods agreed well with each another within their uncertainty ranges. The area of the layer was determined by using a high-resolution optical scanner calibrated by Japan Calibration Service System (JCSS) standard scales. The property values of area density were 1.84 ± 0.05 μg/mm2 for Au, 8.69 ± 0.17 μg/mm2 for Ni, and 8.80 ± 0.14 μg/mm2 for Cu (mean ± expanded uncertainty, coverage factor k = 2). In order to assess the reliability of these values, the density of each metal layer calculated from the property values of the area density and layer thickness measured by using a scanning electron microscope were compared with available literature values and good agreement between the observed values and values obtained in previous studies.