Interaction of polyhydroxy fullerenes with ferrihydrite: adsorption and aggregation.

The rapid development of nanoscience and nanotechnology, with thousands types of nanomaterials being produced, will lead to various environmental impacts. Thus, understanding the behaviors and fate of these nanomaterials is essential. This study focused on the interaction between polyhydroxy fullerenes (PHF) and ferrihydrite (Fh), a widespread iron (oxyhydr)oxide nanomineral and geosorbent. Our results showed that PHF were effectively adsorbed by Fh. The adsorption isotherm fitted the D-R model well, with an adsorption capacity of 67.1mg/g. The adsorption mean free energy of 10.72kJ/mol suggested that PHF were chemisorbed on Fh. An increase in the solution pH and a decrease of the Fh surface zeta potential were observed after the adsorption of PHF on Fh; moreover, increasing initial solution pH led to a reduction of adsorption. The Fourier transform infrared spectra detected a red shift of C-O stretching from 1075 to 1062cm-1 and a decrease of Fe-O bending, implying the interaction between PHF oxygenic functional groups and Fh surface hydroxyls. On the other hand, PHF affected the aggregation and reactivity of Fh by changing its surface physicochemical properties. Aggregation of PHF and Fh with individual particle sizes increasing from 2nm to larger than 5nm was measured by atomic force microscopy. The uniform distribution of C and Fe suggested that the aggregates of Fh were possibly bridged by PHF. Our results indicated that the interaction between PHF and Fh could evidently influence the migration of PHF, as well as the aggregation and reactivity of Fh.