Physical-chemical properties of dental composites and adhesives containing silane-modified SBA-15.

The aim of this study was to synthesize and characterize mesoporous materials SBA-15 and SBA-15 modified with 3-(methacryloxy)-propyl-trimethoxysilane (MPS) to be used as inorganic filler in restorative dental composites and adhesives, and evaluate the main physical-chemical properties of the resulting material. The SBA-15 and SBA-15/MPS were characterized by FTIR, BET and X-Ray and combined with TEGDMA, bis-GMA and commercial spherical silica to produce dental composites. Afterwards, the mesoporous materials were combined with TEGDMA, bis-GMA and HEMA to make adhesives. To compare the results, composites and adhesives containing only commercial spherical silica were investigated. Some physical-chemical properties such as degree of conversion (DC), flexural strength (FS) and modulus (FM), water sorption and solubility (Wsp and Wsl ), specific area (BET), and the leachable components were evaluated. The SBA-15/MPS can be used to prepare dental restorative materials, with some foreseeable advantages compared with pure SBA-15 dental materials and with improved properties compared with commercial spherical silica dental materials. An important improvement was that the dental materials based on modified SBA-15 presented a reduction of approximately 60% in leaching of unreacted monomers extracted by solvent compared to the control group.