In vitro resistance to fracture of two nickel-titanium rotary instruments made with different thermal treatments.
Annali di Stomatologia 2017 April
Aim: Aim of the study was to evaluate effectiveness of different heat treatments in improving Ni-Ti endodontic rotary instruments' resistance to fracture.
Methods: 24 new NiTi instruments similar in length and shape: 12 M3 instruments, tip size 25 and .06 taper (United Dental, Shanghai, China), and 12 M3 Pro Gold instruments tip size 25 and .06 taper (United Dental, Shanghai, China), were tested in a 60° curved artificial root canal. Each group received a different heat treatment. Cycles to fracture were calculated for each instrument. Differences among groups were evaluated with an analysis of variance test (significance level was set at P<0.05.).
Results: Statistical analysis found significant differences (p<0.0213) between groups. The M3 Pro Gold instruments were significantly more resistant to fatigue (mean values = 1012, SD +/- 77) than M3 instruments (mean values = 748, SD +/- 62). No statistically significant differences were found between fragments' lengths (p>0,05).
Conclusions: An increased flexibility and the reduction of internal defects produced by heat treatments during or after manufacturing processes, may be responsible for improving resistance to cyclic fatigue and flexural stresses.
Methods: 24 new NiTi instruments similar in length and shape: 12 M3 instruments, tip size 25 and .06 taper (United Dental, Shanghai, China), and 12 M3 Pro Gold instruments tip size 25 and .06 taper (United Dental, Shanghai, China), were tested in a 60° curved artificial root canal. Each group received a different heat treatment. Cycles to fracture were calculated for each instrument. Differences among groups were evaluated with an analysis of variance test (significance level was set at P<0.05.).
Results: Statistical analysis found significant differences (p<0.0213) between groups. The M3 Pro Gold instruments were significantly more resistant to fatigue (mean values = 1012, SD +/- 77) than M3 instruments (mean values = 748, SD +/- 62). No statistically significant differences were found between fragments' lengths (p>0,05).
Conclusions: An increased flexibility and the reduction of internal defects produced by heat treatments during or after manufacturing processes, may be responsible for improving resistance to cyclic fatigue and flexural stresses.
Full text links
Related Resources
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app
All material on this website is protected by copyright, Copyright © 1994-2024 by WebMD LLC.
This website also contains material copyrighted by 3rd parties.
By using this service, you agree to our terms of use and privacy policy.
Your Privacy Choices 
You can now claim free CME credits for this literature searchClaim now
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app