Tribological properties of PVA/PVP blend hydrogels against articular cartilage.
Journal of the Mechanical Behavior of Biomedical Materials 2018 Februrary
This research investigated in-vitro tribological performance of the articulation of cartilage-on- polyvinyl alcohol (PVA) and polyvinyl pyrrolidone (PVP) blend hydrogels using a custom-designed multi-directional wear rig. The hydrogels were prepared by repeated freezing-thawing cycles at different concentrations and PVA to PVP fractions at a given concentration. PVA/PVP blend hydrogels showed low coefficient of friction (COF) values (between 0.12 ± 0.01 and 0.14 ± 0.02) which were closer to the cartilage-on-cartilage articulation (0.03 ± 0.01) compared to the cartilage-on-stainless steel articulation (0.46 ± 0.06). The COF increased with increasing hydrogel concentration (p = 0.03) and decreasing PVP content at a given concentration (p < 0.05). The cartilage-on-hydrogel tests showed only the surface layers of the cartilage being removed (average volume loss of the condyles was 12.5 ± 4.2mm3 ). However, the hydrogels were found to be worn/deformed. The hydrogels prepared at a higher concentration showed lower apparent volume loss. A strong correlation (R2 = 0.94) was found between the COF and compressive moduli of the hydrogel groups, resulting from decreasing contact congruency. It was concluded that the hydrogels were promising as hemiarthroplasty materials, but that improved mechanical behaviour was required for clinical use.
Full text links
Related Resources
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app
All material on this website is protected by copyright, Copyright © 1994-2024 by WebMD LLC.
This website also contains material copyrighted by 3rd parties.
By using this service, you agree to our terms of use and privacy policy.
Your Privacy Choices
You can now claim free CME credits for this literature searchClaim now
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app