Microstructural Modification and Characterization of Sericite.

Activated sericite was prepared by thermal modification, acid activation and sodium modification, and it was characterized by X-ray diffraction (XRD) analysis, differential scanning calorimetry (DSC), N₂ adsorption test, thermo-gravimetric analysis (TGA), nuclear magnetic resonance (NMR), and scanning electron microscope (SEM). The results indicated that the crystallinity of raw sericite decreased after thermal modification; the pores with sizes between 5 nm to 10 nm of thermal-modified sericite have collapsed and the surface area increased after thermal modification. The dissolving-out amount of Al3+ reached ca. 31 mg/g in the optimal processing conditions during acid activation; cation exchange capacity (CEC) of acid-treated sericite increased to 56.37 mmol/100 g meq/g after sodium modification compared with that of raw sericite (7.42 mmol/100 g). The activated sericite is a promising matrix for clay-polymer nanocomposites.