A Study of the Curing and Flammability Properties of Bisphenol A Epoxy Diacrylate Resin Utilizing a Novel Flame Retardant Monomer, bis[di-acryloyloxyethyl]-p-tert-butyl-phenyl Phosphate.
Materials 2017 Februrary 21
A UV-curable, flame-retardant monomer, DAPP (bis[di-acryloyloxyethyl]-p-tert-butyl-phenyl-phosphate), was synthesized based on BPDCP (4-tert-butylphenyl-dichloro phosphate) and HEA (2-hydroxy ethyl acrylate). DAPP was blended with regular bisphenol A epoxy acrylate (BAEA) in various ratios to yield various phosphorus contents. The TGA-IR (thermogravimetric analyzer interface with an infrared spectrometer) results demonstrate that compounding 30 mol % DAPP with BAEA significantly reduced the amount of released CO gas. In contrast, the peak intensity of CO₂ is independent of phosphorus content. The limiting oxygen index (LOI), reaching the saturated value of 26, and the heat release rate (HRR) measured using a cone-calorimeter, 156.43 KW/m², confirm the saturation point when 30 mol % DAPP was compounded into BAEA. A study of the kinetics of pyrolysis reveals that Ea decreases as the phosphorus content increases. Both the TGA-IR and pyrolysis results reveal that the phosphorus compound DAPP is easily decomposed during the initial stage of burning to form an insulating layer, which inhibits further burning of the resin and the consequent release of other flammable gases.
Full text links
Related Resources
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app
All material on this website is protected by copyright, Copyright © 1994-2024 by WebMD LLC.
This website also contains material copyrighted by 3rd parties.
By using this service, you agree to our terms of use and privacy policy.
Your Privacy Choices
You can now claim free CME credits for this literature searchClaim now
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app