Nanosheets of Two-Dimensional Magnetic and Conducting Fe(II)/Fe(III) Mixed-Valence Metal-Organic Frameworks.

We report the synthesis, magnetic properties, electrical conductivity, and delamination into thin nanosheets of two anilato-based Fe(II)/Fe(III) mixed-valence two-dimensional metal-organic frameworks (MOFs). Compounds [(H3 O)(H2 O)(phenazine)3 ][FeII FeIII (C6 O4 X2 )3 ]·12H2 O [X = Cl (1) and Br (2)] present a honeycomb layered structure with an eclipsed packing that generates hexagonal channels containing the water molecules. Both compounds show ferrimagnetic ordering at ca. 2 K coexisting with electrical conductivity (with room temperature conductivities of 0.03 and 0.003 S/cm). Changing the X group from Cl to Br leads to a decrease in the ordering temperature and room temperature conductivity that is correlated with the decrease of the electronegativity of X. Despite the ionic charge of the anilato-based layers, these MOFs can be easily delaminated in thin nanosheets with the thickness of a few monolayers.