Effect of Final Irrigation Protocol and Etching Mode on Bond Strength of a Multimode Adhesive in the Root Canal.
Journal of Adhesive Dentistry 2017 June 9
PURPOSE: To analyze the effects of ethanol for final post space irrigation and etching mode on the bond strength of fiber posts luted with a mild multimode adhesive (pH 2.3) as compared with a reference group using a self-adhesive resin cement (SAR).
MATERIALS AND METHODS: Human anterior teeth were endodontically treated. After post space preparation, the root canals were irrigated using 1% sodium hypochlorite (NaOCl) applied with passive ultrasonic irrigation, followed by either distilled water (control) or distilled water and ethanol 99% as final post space irrigation. Fiber posts were luted using Futurabond U in self-etch mode (FU-SE), Futurabond U in etch-and-rinse mode (FU-ER), or Futurabond DC (SE) in combination with a dual-curing core buildup material (Grandio Core, all VOCO); alternatively, posts were inserted using a self-adhesive composite cement (RelyX Unicem 2, 3M ESPE). Bond strengths were evaluated using push-out tests following thermocycling (TC) and storage in 0.9% NaCl for 3 months.
RESULTS: Mean push-out bond strengths (MPa) were significantly affected by the luting system (p < 0.0005) but not by the irrigation protocol (p = 0.068; ANOVA), although a significant interaction between the factors "luting agent" and "pre-treatment" was observed. FU E&R (21.28 [4.34]) and RX (20.12 [7.32]) revealed significantly higher bond strengths compared to FU SE (15.9 [6.02]), whereas F DC (18.8 [6.9]) did not differ significantly from all other groups. Ethanol pre-treatment increased bond strength in the apical part of the root canal for all materials, with the exception of FU E&R.
CONCLUSION: Mild multimode adhesives exhibit comparable mean bond strengths to a SAR cement within the root canal for luting fiber posts if applied in an etch-and-rinse mode. Using this approach, ethanol application has no positive effects on bond strength.
MATERIALS AND METHODS: Human anterior teeth were endodontically treated. After post space preparation, the root canals were irrigated using 1% sodium hypochlorite (NaOCl) applied with passive ultrasonic irrigation, followed by either distilled water (control) or distilled water and ethanol 99% as final post space irrigation. Fiber posts were luted using Futurabond U in self-etch mode (FU-SE), Futurabond U in etch-and-rinse mode (FU-ER), or Futurabond DC (SE) in combination with a dual-curing core buildup material (Grandio Core, all VOCO); alternatively, posts were inserted using a self-adhesive composite cement (RelyX Unicem 2, 3M ESPE). Bond strengths were evaluated using push-out tests following thermocycling (TC) and storage in 0.9% NaCl for 3 months.
RESULTS: Mean push-out bond strengths (MPa) were significantly affected by the luting system (p < 0.0005) but not by the irrigation protocol (p = 0.068; ANOVA), although a significant interaction between the factors "luting agent" and "pre-treatment" was observed. FU E&R (21.28 [4.34]) and RX (20.12 [7.32]) revealed significantly higher bond strengths compared to FU SE (15.9 [6.02]), whereas F DC (18.8 [6.9]) did not differ significantly from all other groups. Ethanol pre-treatment increased bond strength in the apical part of the root canal for all materials, with the exception of FU E&R.
CONCLUSION: Mild multimode adhesives exhibit comparable mean bond strengths to a SAR cement within the root canal for luting fiber posts if applied in an etch-and-rinse mode. Using this approach, ethanol application has no positive effects on bond strength.
Full text links
Related Resources
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app
All material on this website is protected by copyright, Copyright © 1994-2024 by WebMD LLC.
This website also contains material copyrighted by 3rd parties.
By using this service, you agree to our terms of use and privacy policy.
Your Privacy Choices
You can now claim free CME credits for this literature searchClaim now
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app