CuV 2 S 4 : A High Rate Capacity and Stable Anode Material for Sodium Ion Batteries.
ACS Applied Materials & Interfaces 2017 June 29
The ternary compound CuV2 S4 exhibits an excellent performance as anode material for sodium ion batteries with a high reversible capacity of 580 mAh g-1 at 0.7 A g-1 after 300 cycles. A Coulombic efficiency of ≈99% is achieved after the third cycle. Increase of the C-rate leads to a drop of the capacity, but a full recovery is observed after switching back to the initial C-rate. In the early stages of Na uptake first Cu+ is reduced and expelled from the electrode as nanocrystalline metallic Cu. An increase of the Na content leads to a full conversion of the material with nanocrystalline Cu particles and elemental V embedded in a Na2 S matrix. The formation of Na2 S is evidenced by 23 Na MAS NMR spectra and X-ray powder diffraction. During the charge process the nanocrystalline Cu particles are retained, but no crystalline materials are formed. At later stages of cycling the reaction mechanism changes which is accompanied by the formation of copper(I) sulfide. The presence of nanocrystalline metallic Cu and/or Cu2 S improves the electrical conductivity, leading to superior cycling and rate capability.
Full text links
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app
All material on this website is protected by copyright, Copyright © 1994-2024 by WebMD LLC.
This website also contains material copyrighted by 3rd parties.
By using this service, you agree to our terms of use and privacy policy.
Your Privacy Choices
You can now claim free CME credits for this literature searchClaim now
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app