Influence of clinical use on physical-structural surface properties and electrochemical potential of NiTi endodontic instruments.

AIM: To investigate the surface morphology and electrochemical potential of superelastic (SE), M-Wire (MW) and shape memory technology (SMT) NiTi instruments before and after single clinical use in vivo.

METHODOLOGY: A total of 60 ProTaper Universal F2 (PTU-SE), ProTaper Next X2 (PTN-MW), Typhoon (TYP), Hyflex (HF) and Vortex Blue (VB), the last three SMT, and size 25, .06 taper (n = 6 of each type) files were examined. Scanning electron microscopy (SEM), X-ray energy-dispersive spectroscopy (EDS) and electrochemical potential analysis were employed before and after clinical use. Statistical analysis was performed with one-way analysis of variance and Bonferroni's post hoc test. Significance was determined at the 95% confidence level for both tests.

RESULTS: SEM observations of new instruments indicated the presence of marks left by the machining process during manufacturing and EDS revealed the existence of an oxide coating on shape memory instruments. After clinical use, the five types were associated with propagation of transverse cracks 3 mm from the tip. The surface oxide layer of TYP, HF and VB instruments had microcracks in multiple directions, whilst TYP and HF had fragmentation in chip form of the oxide layer. EDS analysis demonstrated a significant reduction of the oxide layer in shape memory instruments, except for VB. Electrochemical potentials were higher for shape memory instruments than for M-Wire and superelastic NiTi instruments, respectively (P < 0.05).

CONCLUSIONS: It appears that shape memory technology NiTi instruments have a dysfunctional oxide layer after clinical use. Additionally, they featured higher electrochemical potential relative to NiTi instruments manufactured from M-Wire, and conventional superelastic NiTi alloy.

Full text links

We have located links that may give you full text access.
Can't access the paper?
Try logging in through your university/institutional subscription. For a smoother one-click institutional access experience, please use our mobile app.

For the best experience, use the Read mobile app

Mobile app image

Get seemless 1-tap access through your institution/university

For the best experience, use the Read mobile app

All material on this website is protected by copyright, Copyright © 1994-2024 by WebMD LLC.
This website also contains material copyrighted by 3rd parties.

By using this service, you agree to our terms of use and privacy policy.

Your Privacy Choices Toggle icon

You can now claim free CME credits for this literature searchClaim now

Get seemless 1-tap access through your institution/university

For the best experience, use the Read mobile app