Annealing Stability Study of Co 20 Fe 60 B 20 \MgO\ Co 20 Fe 60 B 20 Perpendicular Magnetic Tunnel Junctions.

A full Co20 Fe60 B20 \MgO\ Co20 Fe60 B20 perpendicular magnetic tunnel junction (pMTJ) with (Co\Pt) multilayers as pinning layers and different functional multilayers stacks were made and annealed at different temperatures. The tunneling magnetoresistance ratio (TMR) and MgO barrier resistance-area product (RA) were measured and analyzed as a function of annealing temperature. The TMR of pMTJs dramatically declines with increasing annealing temperatures from 320 °C to 400 °C while the RA increases with temperature from 375 °C to 450 °C. The pMTJs and partial stacks were also measured in a vibrating sample magnetometer (VSM). We found that the (Co\Pt) multilayers are very stable and maintain a magnetization direction perpendicular to the film plane up to 450 °C. However, the magnetization direction of the CoFeB above and below the MgO barrier rotates from perpendicular to in-plane with increasing annealing temperature. Furthermore, the CoFeB layer influences the adjacent (Co\Pt) layers to rotate at the same time. The pMTJs' elemental depth profiles in the as deposited and annealed states were determined by Secondary Ion Mass Spectrometry (SIMS). We found that Boron and Tantalum migrate towards the top of the stack. The other elements (Platinum, Cobalt, Ruthenium, and Magnesium) are very stable and do not interdiffuse during annealing up to 450°C.

Full text links

We have located links that may give you full text access.
Can't access the paper?
Try logging in through your university/institutional subscription. For a smoother one-click institutional access experience, please use our mobile app.

For the best experience, use the Read mobile app

Mobile app image

Get seemless 1-tap access through your institution/university

For the best experience, use the Read mobile app

All material on this website is protected by copyright, Copyright © 1994-2024 by WebMD LLC.
This website also contains material copyrighted by 3rd parties.

By using this service, you agree to our terms of use and privacy policy.

Your Privacy Choices Toggle icon

You can now claim free CME credits for this literature searchClaim now

Get seemless 1-tap access through your institution/university

For the best experience, use the Read mobile app