Separation and recovery of glass, plastic and indium from spent LCD panels.

The present paper deals with physico-mechanical pre-treatments for dismantling of spent liquid crystal displays (LCDs) and further recovery of valuable fractions like plastic, glass and indium. After a wide experimental campaign, two processes were designed, tested and optimized. In the wet process, 20%, 15% and 40% by weight of the feeding panels are recovered as plastic, glass and indium concentrate, respectively. Instead, in the dry process, only two fractions were separated: around 11% and 85% by weight are recovered as plastic and glass/indium mixture. Indium, that concentrated in the -212μm fraction, was completely dissolved by sulphuric acid leaching (0.75molL(-1) H2SO4 solution, 80°C, 10%vol H2O2, pulp density 10%wt/vol, leaching time 3h). 100% of indium can be extracted from the pregnant solution with 5%wt/vol Amberlite™ resin, at room temperature and pH 3 in 24h. Indium was thus re-extracted from the resin by means of a 2molL(-1) H2SO4 solution, at room temperature and S/L of 40%wt/vol.