Cellulose oxidation by Laccase-TEMPO treatments.

In this work, laccase-TEMPO (Lac-T) treatments were applied to bleached commercial dissolving pulp in order to introduce carbonyl and carboxyl groups, which were found to improve dry and wet strength-related properties. Also the solubility behavior towards xanthate reactions was assessed. The effect of a refining step (R) before the oxidative treatment, the absence or presence of oxygen pressure, TEMPO dose (2 or 8% oven dried pulp) and reaction time (8 or 20h) were thoroughly examined. Treatments conducted in the presence of oxygen pressure exhibited greater amount of functional groups. Introducing a pre-refining treatment resulted in similar functional groups but higher wet strength was achieved. Specifically, a high W/D strength ratio was observed, indicating that wet strength-related property was satisfactorily developed. Besides the fact that all Lac-T treatments caused severe cellulose degradation, no fiber strength loss was detected. In fact, all oxidized samples presented higher Wet Zero-Span Tensile Strength, mainly in R+ Lac-T (O2 ) sample, which suggested the formation of hemiacetal linkages between the new introduced aldehyde groups and available free hydroxyl groups resulting from fibrillation.