Effect of Repeated Firings on Microtensile Bond Strength of Bi-layered Lithium Disilicate Ceramics (e.max CAD and e.max Press).

AIM: To achieve acceptable contour, color, esthetics, and occlusal relations, the porcelain may be subjected to several firing cycles. This study sought to assess the effect of multiple firing cycles on the microtensile bond strength (MTBS) of lithium disilicate-based ceramics (e.max Press, e.max CAD).

MATERIALS AND METHODS: IPS e.max computer aided design (CAD) cores were fabricated using CAD/(Computer Aided Manufacturing (CAM)) technology, and IPS e.max Press cores were fabricated using the heat-pressing technique (12 × 12 × 4 mm(3)). Cores in each group were divided into three subgroups based on the number of firing cycles (three, five, and seven cycles). After porcelain application, the samples were sectioned into microbars and a total of 20 sound microbars in each group were subjected to tensile load in a microtensile tester at a crosshead speed of 1 mm/minute. Microtensile bond strength of the core to the veneering porcelain was analyzed using one-way analysis of variance (ANOVA). Pairwise comparisons were made using the Tukey's test (p < 0.05).

RESULTS: In the e.max CAD, the mean MTBS values were 22.07 ± 6.63, 34.68 ± 7.07, and 26.05 ± 10.29 MPa following three, five, and seven firing cycles respectively. These values for the e.max Press were 34.46 ± 9.28, 23.09 ± 5.02, and 31.26 ± 12.25 MPa respectively. There was significant difference in bond strength of e.max CAD (p < 0.003) and e.max Press (p < 0.002) based on the number of firing cycles.

CONCLUSION: Increasing the number of porcelain firing cycles decreased the bond strength of the core to the veneering porcelain in both ceramics.

CLINICAL SIGNIFICANCE: It is better to decrease the number of firing cycle as much as possible.

Full text links

We have located links that may give you full text access.
Can't access the paper?
Try logging in through your university/institutional subscription. For a smoother one-click institutional access experience, please use our mobile app.

For the best experience, use the Read mobile app

Mobile app image

Get seemless 1-tap access through your institution/university

For the best experience, use the Read mobile app

All material on this website is protected by copyright, Copyright © 1994-2024 by WebMD LLC.
This website also contains material copyrighted by 3rd parties.

By using this service, you agree to our terms of use and privacy policy.

Your Privacy Choices Toggle icon

You can now claim free CME credits for this literature searchClaim now

Get seemless 1-tap access through your institution/university

For the best experience, use the Read mobile app