Characterisation and microleakage of a new hydrophilic fissure sealant - UltraSeal XT® hydro™.

OBJECTIVES: The aim of this study was to characterise the new hydrophilic fissure sealant, UltraSeal XT® hydro™ (Ultradent Products, USA), and to investigate its in vitro resistance to microleakage after placement on conventionally acid etched and sequentially lased and acid etched molars.

MATERIAL AND METHODS: The sealant was characterised by Fourier transform infra-red spectroscopy (FTIR), scanning electron microscopy (SEM), energy dispersive X-ray analysis (EDX), and Vickers indentation test. Occlusal surfaces of extracted human molars were either conventionally acid etched (n=10), or sequentially acid etched and laser irradiated (n=10). UltraSeal XT® hydro™ was applied to both groups of teeth which were then subjected to 2,500 thermocycles between 5 and 55°C prior to microleakage assessment by fuchsin dye penetration.

RESULTS: UltraSeal XT® hydro™ is an acrylate-based sealant that achieved a degree of conversion of 50.6±2.2% and a Vickers microhardness of 24.2±1.5 under standard light curing (1,000 mWcm-2 for 20 s). Fluoride ion release is negligible within a 14-day period. SEM and EDX analyses indicated that the sealant comprises irregular submicron and nano-sized silicon-, barium-, and aluminium-bearing filler phases embedded in a ductile matrix. Laser preconditioning was found to significantly reduce microleakage (Mann-Whitney U test, p<0.001). The lased teeth presented enhanced surface roughness on a 50 to 100 μm scale that caused the segregation and concentration of the filler particles at the enamel-sealant interface.

CONCLUSION: Laser preconditioning significantly decreased microleakage and increased enamel surface roughness, which caused zoning of the filler particles at the enamel-sealant interface.