Evaluation of the bond strength of root-end placed mineral trioxide aggregate and Biodentine in the absence/presence of blood contamination.

OBJECTIVE: Mineral trioxide aggregate (MTA) has been accepted as an appropriate root-end filling material in endodontic microsurgery because of setting ability in the wet environment. The aim of this study was to assess the bond strength of root-end placed MTA and Biodentine (Septodont, Saint Maur des Fossés, France) in the absence/presence of blood contamination.

MATERIALS AND METHODS: Forty-eight single-rooted maxillary incisors were used. subsequent to root-end resection and apical preparation using ultrasonic retro-tips, the specimens were randomly separated into two groups according to the root-end filling materials: MTA (Cerkamed Medical Company, Stalowa, Poland) or Biodentine. The specimens were then separated into two subgroups according to storage condition (absence/presence of blood) (n = 12). After obtaining 2.0 ± 0.1 mm slices, push-out tests were performed. Each slice was examined under a stereomicroscope to evaluate the failure mode. The data were analyzed using two-way analysis of variance and Tukey's post hoc test for multiple comparisons. The failure modes were analyzed using the Chi-square test (P = 0.05).

RESULTS: The bond strength was significantly affected by the presence of blood contamination and root-end filling material type (P < 0.001). Biodentine had better bond strength than MTA (P < 0.001). The most common failure type was adhesive failure. According to the Chi-square test, there were no statistically significant differences among the groups (P = 0.394).

CONCLUSIONS: Biodentine had better bond strength values compared to MTA, and the bond strength of both MTA and Biodentine as root-end filling materials was negatively affected by the presence of blood.