Bond strength and micro-computed tomographic evaluation of pre-coated brackets.
Australian Orthodontic Journal 2015 November
OBJECTIVES: The aim of the present study was to assess and compare the shear bond strength (SBS) of metal pre-coated orthodontic brackets bonded to fluorotic and non-fluorotic teeth treated with three different etching techniques. A second aim was to determine the volume of adhesive remaining on the tooth at debond using micro-computed tomography (μCT).
METHODS: Ninety extracted premolars were selected to include 45 fluorotic (test group) and 45 non-fluorotic (control group) teeth. Each group was divided into three subgroups of 15 each, which were treated as follows: 1) micro-etched; 2) acid-etched; and 3) both micro-etched and acid-etched. A bonding agent was applied to the prepared surfaces; pre-coated and light-cured brackets were attached to all teeth. An Instron universal testing machine was used to record the debonding force. Specimens were then scanned using a microCT to evaluate the amount of adhesive remaining on the teeth. The significance of the statistical tests was pre-determined at p < 0.05.
RESULTS: Two-way ANOVA showed that fluorosis of teeth had no influence on the SBS (p = 0.165) whereas the volume of adhesive remnants was significantly higher in the control group compared with the test group (p < 0.001).
CONCLUSIONS: Fluorosis had no influence on the SBS of brackets, whereas it had a negative influence on retaining adhesives onto the tooth surfaces.
METHODS: Ninety extracted premolars were selected to include 45 fluorotic (test group) and 45 non-fluorotic (control group) teeth. Each group was divided into three subgroups of 15 each, which were treated as follows: 1) micro-etched; 2) acid-etched; and 3) both micro-etched and acid-etched. A bonding agent was applied to the prepared surfaces; pre-coated and light-cured brackets were attached to all teeth. An Instron universal testing machine was used to record the debonding force. Specimens were then scanned using a microCT to evaluate the amount of adhesive remaining on the teeth. The significance of the statistical tests was pre-determined at p < 0.05.
RESULTS: Two-way ANOVA showed that fluorosis of teeth had no influence on the SBS (p = 0.165) whereas the volume of adhesive remnants was significantly higher in the control group compared with the test group (p < 0.001).
CONCLUSIONS: Fluorosis had no influence on the SBS of brackets, whereas it had a negative influence on retaining adhesives onto the tooth surfaces.
Full text links
Related Resources
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app
All material on this website is protected by copyright, Copyright © 1994-2024 by WebMD LLC.
This website also contains material copyrighted by 3rd parties.
By using this service, you agree to our terms of use and privacy policy.
Your Privacy Choices
You can now claim free CME credits for this literature searchClaim now
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app