Effect of immediate and delayed dentin sealing on the fracture strength, failure type and Weilbull characteristics of lithiumdisilicate laminate veneers.
Dental Materials 2016 April
OBJECTIVES: Adhesion on dentin is less reliable than on enamel, which could affect the durability of laminate veneers (LV). Immediate dentin sealing (IDS) is suggested instead of delayed dentin sealing (DDS) to overcome hypersensitivity and prevent debonding from dentin. This study evaluated the effect of IDS and DDS on the durability of Li2Si2O5 laminate veneers in vitro.
METHODS: Window preparations were made on the labial surfaces of sound maxillary central incisors (N=50). They were randomly divided into five groups: Group 1: Enamel only+H3PO4+Adhesive (control); Group 2: <1/4 dentin+H3PO4+DDS (2 weeks later); Group 3: Complete dentin+H3PO4+DDS (2 weeks later); Group 4: <1/4 dentin+H3PO4+IDS; Group 5: Complete dentin+H3PO4+IDS. Li2Si2O5 laminate veneers (e.max Press) were bonded to the labial surfaces of the teeth with adhesive resin cement (Variolink Veneer). IDS layers were silicacoated (CoJet System) and silanized (ESPE-Sil). The teeth with their bonded laminates were thermocycled (10.000× cycles) and then subjected to static loading (1mm/min). Failure type and location after debonding were classified. Data were analyzed using ANOVA and Tukey's post hoc test (α=0.05). Two-parameter Weibull distribution values including the Weibull modulus, scale (m) and shape (0), values were calculated.
RESULTS: Mean fracture strength (N) per group in descending order was as follows: Group 5 (576±254), Group 4 (478±216), Group 1 (473±159), Group 2 (465±186), and Group 3 (314±137). The presence of complete dentin exposure sealed with DDS after 2 weeks on the bonded surface (Group 3) resulted in significantly lower fracture strength results than those in group 5 with IDS (p=0.034). Weibull distribution presented higher shape (0) for Group 1 (3.67), than those of other groups (2.51-2.89). Failure types were predominantly adhesive failure between the cement and the laminate veneer in Groups 1, 2, 4 whereas Group 3 presented more often complete adhesive failures between the cement and dentin. In Group 5, failures showed some IDS and cement with or without ceramic fracture attached on the tooth.
SIGNIFICANCE: When laminate veneers are bonded to a large dentin substrate, application of immediate dentin sealing improves adhesion and thereby, the fracture strength of Li2Si2O5 laminate veneers.
METHODS: Window preparations were made on the labial surfaces of sound maxillary central incisors (N=50). They were randomly divided into five groups: Group 1: Enamel only+H3PO4+Adhesive (control); Group 2: <1/4 dentin+H3PO4+DDS (2 weeks later); Group 3: Complete dentin+H3PO4+DDS (2 weeks later); Group 4: <1/4 dentin+H3PO4+IDS; Group 5: Complete dentin+H3PO4+IDS. Li2Si2O5 laminate veneers (e.max Press) were bonded to the labial surfaces of the teeth with adhesive resin cement (Variolink Veneer). IDS layers were silicacoated (CoJet System) and silanized (ESPE-Sil). The teeth with their bonded laminates were thermocycled (10.000× cycles) and then subjected to static loading (1mm/min). Failure type and location after debonding were classified. Data were analyzed using ANOVA and Tukey's post hoc test (α=0.05). Two-parameter Weibull distribution values including the Weibull modulus, scale (m) and shape (0), values were calculated.
RESULTS: Mean fracture strength (N) per group in descending order was as follows: Group 5 (576±254), Group 4 (478±216), Group 1 (473±159), Group 2 (465±186), and Group 3 (314±137). The presence of complete dentin exposure sealed with DDS after 2 weeks on the bonded surface (Group 3) resulted in significantly lower fracture strength results than those in group 5 with IDS (p=0.034). Weibull distribution presented higher shape (0) for Group 1 (3.67), than those of other groups (2.51-2.89). Failure types were predominantly adhesive failure between the cement and the laminate veneer in Groups 1, 2, 4 whereas Group 3 presented more often complete adhesive failures between the cement and dentin. In Group 5, failures showed some IDS and cement with or without ceramic fracture attached on the tooth.
SIGNIFICANCE: When laminate veneers are bonded to a large dentin substrate, application of immediate dentin sealing improves adhesion and thereby, the fracture strength of Li2Si2O5 laminate veneers.
Full text links
Related Resources
Trending Papers
Challenges in Septic Shock: From New Hemodynamics to Blood Purification Therapies.Journal of Personalized Medicine 2024 Februrary 4
Molecular Targets of Novel Therapeutics for Diabetic Kidney Disease: A New Era of Nephroprotection.International Journal of Molecular Sciences 2024 April 4
The 'Ten Commandments' for the 2023 European Society of Cardiology guidelines for the management of endocarditis.European Heart Journal 2024 April 18
A Guide to the Use of Vasopressors and Inotropes for Patients in Shock.Journal of Intensive Care Medicine 2024 April 14
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app
All material on this website is protected by copyright, Copyright © 1994-2024 by WebMD LLC.
This website also contains material copyrighted by 3rd parties.
By using this service, you agree to our terms of use and privacy policy.
Your Privacy Choices
You can now claim free CME credits for this literature searchClaim now
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app