In-Vitro Comparative Study of In-office and Home Bleaching Agents on Surface Micro-morphology of Enamel.
OBJECTIVE: To evaluate the effect of home-use bleaching agent containing 16% Carbamide Peroxide (CP) and in-office bleaching agent with 38% Hydrogen Peroxide (HP) on surface micro-morphology of enamel.
STUDY DESIGN: An experimental study.
PLACE AND DURATION OF STUDY: The discs were prepared at Material Engineering Department of NED University of Engineering and Technology, Karachi, and surface morphology was analyzed at Centralized Science Laboratory of Karachi University, Pakistan. Duration of study was one year from January to December 2012.
METHODOLOGY: Forty five sound human third molar crowns, extracted for periodontal reason, were included in the study. Longitudinal sections were made using diamond disks (0.2 mm) under water lubrication to obtain enamel slabs measuring (3 mm x 3 mm). The slabs were embedded in polystyrene resin by using 2.0 cm diameter PVC molds, leaving the outer enamel surface uncovered by the resin. Ninety dental enamel slabs were prepared. The slabs were then randomly divided into 3 groups. Each group contained thirty specimens (n=30). Group 1 was kept in artificial saliva at 37°C in incubator (Memart, Germany) during whole experiment. Group 2 was treated with power whitening gel (White Smile 2011, Germany). Group 3 was treated with tooth whitening pen (White Smile 2011, Germany). The most central region or the region that was most representative of the entire surface area was used. The SEM (Jeol-Japan-JSM6380A, JAPAN) micrographs were examined to determine the type of surface presented. The enamel changes were classified as no or mild alteration, moderate alteration and severe altered surface.
RESULTS: Regarding micro-morphology, the enamel surface of control groups showed smooth surface in general with some scattered clear scratches due to the polishing procedure. The specimens bleached in group 2 and group 3, represented areas of mild erosion.
CONCLUSION: Bleaching with 38% Hydrogen Peroxide (HP) and 16% Carbamide Peroxide (CP) resulted in mild changes in surface micro-morphology of enamel.
STUDY DESIGN: An experimental study.
PLACE AND DURATION OF STUDY: The discs were prepared at Material Engineering Department of NED University of Engineering and Technology, Karachi, and surface morphology was analyzed at Centralized Science Laboratory of Karachi University, Pakistan. Duration of study was one year from January to December 2012.
METHODOLOGY: Forty five sound human third molar crowns, extracted for periodontal reason, were included in the study. Longitudinal sections were made using diamond disks (0.2 mm) under water lubrication to obtain enamel slabs measuring (3 mm x 3 mm). The slabs were embedded in polystyrene resin by using 2.0 cm diameter PVC molds, leaving the outer enamel surface uncovered by the resin. Ninety dental enamel slabs were prepared. The slabs were then randomly divided into 3 groups. Each group contained thirty specimens (n=30). Group 1 was kept in artificial saliva at 37°C in incubator (Memart, Germany) during whole experiment. Group 2 was treated with power whitening gel (White Smile 2011, Germany). Group 3 was treated with tooth whitening pen (White Smile 2011, Germany). The most central region or the region that was most representative of the entire surface area was used. The SEM (Jeol-Japan-JSM6380A, JAPAN) micrographs were examined to determine the type of surface presented. The enamel changes were classified as no or mild alteration, moderate alteration and severe altered surface.
RESULTS: Regarding micro-morphology, the enamel surface of control groups showed smooth surface in general with some scattered clear scratches due to the polishing procedure. The specimens bleached in group 2 and group 3, represented areas of mild erosion.
CONCLUSION: Bleaching with 38% Hydrogen Peroxide (HP) and 16% Carbamide Peroxide (CP) resulted in mild changes in surface micro-morphology of enamel.
Full text links
Related Resources
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app
All material on this website is protected by copyright, Copyright © 1994-2024 by WebMD LLC.
This website also contains material copyrighted by 3rd parties.
By using this service, you agree to our terms of use and privacy policy.
Your Privacy Choices 
You can now claim free CME credits for this literature searchClaim now
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app