A comparative evaluation of the effect of dentin desensitizers on the retention of complete cast metal crowns.
Contemporary Clinical Dentistry 2015 March
CONTEXT: Desensitizers are used to reduce dentin hypersensitivity. They affect the surface texture of prepared dentin and may alter the retention of fixed restorations.
AIMS: The aim was to evaluate the effect of dentin desensitizers on the retention of complete cast metal crowns luted with glass ionomer cement.
SUBJECTS AND METHODS: Fifty freshly extracted human premolars were subjected to standardized tooth preparation (20° total convergence, 4 mm axial height) with a computer numerically controlled machine. Individual cast metal crowns were fabricated from a base metal alloy. Dentin desensitizers included none (control), a glutaraldehyde (GLU) based primer (Gluma desensitizer), casein phosphopeptide (CPP)-amorphous calcium phosphate (ACP) (GC Mousse), erbium, chromium: YSGG laser (Waterlase MD Turbo, Biolase) and Pro-Argin (Colgate Sensitive Pro-Relief desensitizing polishing paste). After desensitization, crowns were luted with glass ionomer cement and kept for 48 h at 37°C in 100% relative humidity. The samples were tested using a universal testing machine by applying a load at a crosshead speed of 0.5 mm/min.
STATISTICAL ANALYSIS USED: Statistical analysis included One-way ANOVA, followed by the Scheffe post-hoc test with P < 0.05.
RESULTS: All dentin desensitizers showed significantly different values: Pro-Argin (4.10 Megapascals [Mpa]) < CPP-ACP (4.01 mpa) < GLU based primer (3.87 Mpa) < Virgin dentin (3.65 Mpa) < LASER (3.37 Mpa).
CONCLUSIONS: On comparing the effect of prepared virgin dentin, GLU based primer, CPP-ACP, LASER and Pro-Argin on the retention of complete cast metal crowns luted with glass ionomer cement on prepared teeth, it can be concluded that Pro-Argin and CPP-ACP showed the best retention in this in vitro study.
AIMS: The aim was to evaluate the effect of dentin desensitizers on the retention of complete cast metal crowns luted with glass ionomer cement.
SUBJECTS AND METHODS: Fifty freshly extracted human premolars were subjected to standardized tooth preparation (20° total convergence, 4 mm axial height) with a computer numerically controlled machine. Individual cast metal crowns were fabricated from a base metal alloy. Dentin desensitizers included none (control), a glutaraldehyde (GLU) based primer (Gluma desensitizer), casein phosphopeptide (CPP)-amorphous calcium phosphate (ACP) (GC Mousse), erbium, chromium: YSGG laser (Waterlase MD Turbo, Biolase) and Pro-Argin (Colgate Sensitive Pro-Relief desensitizing polishing paste). After desensitization, crowns were luted with glass ionomer cement and kept for 48 h at 37°C in 100% relative humidity. The samples were tested using a universal testing machine by applying a load at a crosshead speed of 0.5 mm/min.
STATISTICAL ANALYSIS USED: Statistical analysis included One-way ANOVA, followed by the Scheffe post-hoc test with P < 0.05.
RESULTS: All dentin desensitizers showed significantly different values: Pro-Argin (4.10 Megapascals [Mpa]) < CPP-ACP (4.01 mpa) < GLU based primer (3.87 Mpa) < Virgin dentin (3.65 Mpa) < LASER (3.37 Mpa).
CONCLUSIONS: On comparing the effect of prepared virgin dentin, GLU based primer, CPP-ACP, LASER and Pro-Argin on the retention of complete cast metal crowns luted with glass ionomer cement on prepared teeth, it can be concluded that Pro-Argin and CPP-ACP showed the best retention in this in vitro study.
Full text links
Related Resources
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app
All material on this website is protected by copyright, Copyright © 1994-2024 by WebMD LLC.
This website also contains material copyrighted by 3rd parties.
By using this service, you agree to our terms of use and privacy policy.
Your Privacy Choices
You can now claim free CME credits for this literature searchClaim now
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app