Adhesion of resin-modified glass-ionomer cements may affect the integrity of tooth structure in the open sandwich technique.
Dental Materials 2014 December
OBJECTIVE: To study the interfaces between model cavities prepared in teeth and four glass ionomer cements (two conventional and two resin-modified).
METHODS: Ten non-cavitated molars and premolars were used and, in each, two 3mm deep slot preparations were created on opposing sides of the tooth. The teeth were conditioned as appropriate, then restored using the open sandwich technique, using a conventional glass ionomer (Fuji IX, Ketac Molar) or resin modified glass ionomer (Fuji II LC or N100), followed by completion with composite resin. The teeth were then embedded in a transparent acrylic resin and cut parallel to the long axis through both restorations, using a low speed diamond wheel saw. Samples were evaluated using a metallographic light microscope (100×). Three areas were assessed: the axial wall, the axial gingival line angle and the cavo-surface line angle. Bonding was categorized as inadequate or adequate based on the appearance and inadequate bonding was further studied and classified. Data were analysed statistically using the McNamara analysis.
RESULTS: The majority of materials failed to make adequate contact with the axial wall, and there were also flaws at the axial/gingival line angle in several samples. By contrast, the cavo-surface line angle was generally soundly filled and the materials showed intimate contact with the tooth surface in this region. The most serious inadequacy, though, was not lack of intimate contact and/or adhesive bond, but the presence of perpendicular cracks in 30% of the Fuji II LC samples which extended into the underlying dentin.
SIGNIFICANCE: The problems of placement and dentin cracking experienced with these materials demonstrate that adhesive bond strength alone cannot be used as the criterion of success for restorative materials. In fact good adhesion can, in certain cases, promote cracking of the dentin due to stresses within the material, an outcome which is undesirable.
METHODS: Ten non-cavitated molars and premolars were used and, in each, two 3mm deep slot preparations were created on opposing sides of the tooth. The teeth were conditioned as appropriate, then restored using the open sandwich technique, using a conventional glass ionomer (Fuji IX, Ketac Molar) or resin modified glass ionomer (Fuji II LC or N100), followed by completion with composite resin. The teeth were then embedded in a transparent acrylic resin and cut parallel to the long axis through both restorations, using a low speed diamond wheel saw. Samples were evaluated using a metallographic light microscope (100×). Three areas were assessed: the axial wall, the axial gingival line angle and the cavo-surface line angle. Bonding was categorized as inadequate or adequate based on the appearance and inadequate bonding was further studied and classified. Data were analysed statistically using the McNamara analysis.
RESULTS: The majority of materials failed to make adequate contact with the axial wall, and there were also flaws at the axial/gingival line angle in several samples. By contrast, the cavo-surface line angle was generally soundly filled and the materials showed intimate contact with the tooth surface in this region. The most serious inadequacy, though, was not lack of intimate contact and/or adhesive bond, but the presence of perpendicular cracks in 30% of the Fuji II LC samples which extended into the underlying dentin.
SIGNIFICANCE: The problems of placement and dentin cracking experienced with these materials demonstrate that adhesive bond strength alone cannot be used as the criterion of success for restorative materials. In fact good adhesion can, in certain cases, promote cracking of the dentin due to stresses within the material, an outcome which is undesirable.
Full text links
Related Resources
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app
All material on this website is protected by copyright, Copyright © 1994-2024 by WebMD LLC.
This website also contains material copyrighted by 3rd parties.
By using this service, you agree to our terms of use and privacy policy.
Your Privacy Choices
You can now claim free CME credits for this literature searchClaim now
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app