Polishing and coating carbon fiber-reinforced carbon composites with a carbon-titanium layer enhances adhesion and growth of osteoblast-like MG63 cells and vascular smooth muscle cells in vitro.
Journal of Biomedical Materials Research 2001 March 16
Carbon fiber-reinforced carbon composites (CFRC) are considered to be promising materials for orthopedic and dental surgery. Their mechanical properties can be tailored to be similar to those of bone, and their chemical composition (close to pure carbon) promises that they will be tolerated well by the surrounding tissue. In this study, CFRC composites were fabricated from phenolic resin and unidirectionally oriented Torayca carbon fibers by carbonization (1000 degrees C) and graphitization (2500 degrees C). The material then was cut with a diamond saw into sheets of 8 x 10 x 3 mm, and the upper surface was polished by colloidal SiO2 and/or covered with a carbon-titanium (C:Ti) layer (3.3 microm) using the plasma-enhanced physical vapor deposition method. Three different kinds of modified samples were prepared: polished only, covered only, and polished + covered. Untreated samples served as a control. The surface roughness of these samples, measured by a Talysurf profilometer, decreased significantly after polishing but usually did not decrease after coating with a C:Ti layer. On all three modified surfaces, human osteoblast-like cells of the MG63 line and rat vascular smooth muscle cells (both cultured in a Dulbecco's minimum essential medium with 10% fetal bovine serum) adhered at higher numbers (by 21-87% on day 1 after seeding) and exhibited a shorter population doubling time (by 13-40%). On day 4 after seeding, these cells attained higher population densities (by 61-378%), volume (by 18-37%), and protein content (by 16-120%). These results were more pronounced in VSMC than in MG63 cells and in both groups of C:Ti-covered samples than in the polished only samples. The release of carbon particles from the CFRC composites was significantly decreased--by 8 times in the polished only, 24 times in the covered only, and 42 times in the polished + covered samples. These results show that both polishing and carbon-titanium covering significantly improve the biocompatibility of CFRC composites in vitro, especially when these two modifications are combined.
Full text links
Related Resources
Trending Papers
Challenges in Septic Shock: From New Hemodynamics to Blood Purification Therapies.Journal of Personalized Medicine 2024 Februrary 4
Molecular Targets of Novel Therapeutics for Diabetic Kidney Disease: A New Era of Nephroprotection.International Journal of Molecular Sciences 2024 April 4
Perioperative echocardiographic strain analysis: what anesthesiologists should know.Canadian Journal of Anaesthesia 2024 April 11
The 'Ten Commandments' for the 2023 European Society of Cardiology guidelines for the management of endocarditis.European Heart Journal 2024 April 18
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app
All material on this website is protected by copyright, Copyright © 1994-2024 by WebMD LLC.
This website also contains material copyrighted by 3rd parties.
By using this service, you agree to our terms of use and privacy policy.
Your Privacy Choices
You can now claim free CME credits for this literature searchClaim now
Get seemless 1-tap access through your institution/university
For the best experience, use the Read mobile app