Ceramic thickness and bond strength

STATEMENT OF PROBLEM: Dental cobalt-chromium (Co-Cr) alloy manufactured by selective laser melting (SLM) is not recommended for clinical applications before annealing because of excessive residual stress. However, limited information is available regarding the relationship between annealing temperature and the metal-ceramic bond properties of SLM Co-Cr alloys. PURPOSE: The purpose of this in vitro study was to investigate the effects of annealing temperature on the metal-ceramic bond properties of SLM Co-Cr alloys...

The cementation of indirect restoration is one of the most important steps in prosthetic and restorative dentistry. Cementation aims to bond the prosthetic restoration to the prepared enamel or enamel and dentine. Successful cementation protocols prevent biofilm formation at the margin between tooth and restoration and minimize mechanical and biological complications. With the advancements in dental cements, they have been modified to be versatile in terms of handling, curing, and bond strengths. This review presents updates on dental cements, focusing on the composition, properties, advantages, limitations, and indications of the various cements available...

The aim of this study was to evaluate the effect of different surface treatments combined with laser irradiation on the shear bond strength of different CAD-CAM ceramics to composite resin. A total of hundred forty-seven ceramic specimens with thicknesses of 2.5 mm were prepared from three different CAD-CAM ceramics (an yttrium oxide partially stabilized tetragonal zirconia polycrystal (Y-TZP); a zirconia-reinforced lithium silicate glass ceramic (ZLS); and a lithium disilicate-strengthened lithium aluminosilicate glass ceramic (LD-LAS)) and subjected to seven groups of treatment (n = 7): (1) control (no treatment), (2) Er:YAG laser irradiation, (3) Nd:YAG laser irradiation, (4) etching with hydrofluoric acid (HFA), (5) Er:YAG + HFA, (6) Nd:YAG + HFA, and (7) sandblasting...

Precursor-derived silicoboron carbonitride ceramic (PDC-SiBCN) has attracted significant attention as an advanced electromagnetic (EM) wave-absorbing material. However, the inherent porous and brittle characteristics limit its application as a structural load component in an EM interference environment. In this study, phase-transformation HfO2 nanoparticles were incorporated into PDC-SiBCN to reduce volume shrinkage, improve bonding interactions, and control structural defects, simultaneously boosting the plastic deformation and EM performance of brittle ceramics...

OBJECTIVES:  This in vitro study was performed to evaluate fatigue survival by shear test in the union of leucite-reinforced feldspathic ceramic using different cement thicknesses. MATERIALS AND METHODS:  Leucite-reinforced glass ceramics blocks were sectioned in 2-mm thick slices where resin cylinders were cemented. The samples were distributed in two experimental groups ( n  = 20) according to the cement thickness (60 and 300 μm)...

STATEMENT OF PROBLEM: Selective laser melting has been increasingly used in the fabrication of metal-ceramic prostheses. The longevity of the prostheses depends on the strength of the metal-ceramic bond, which may differ with the framework manufacturing technique. PURPOSE: The purpose of this in vitro study was to compare the bond strength of ceramic to cobalt-chromium (Co-Cr) alloys fabricated by different manufacturing methods. MATERIAL AND METHODS: Sixty Ø15×2-mm disk-shaped specimens were prepared and assigned to 3 groups (n=20) with different manufacturing methods: milled Co-Cr (M), selective laser melted Co-Cr (SLM), and cast Co-Cr (C)...

PURPOSE: To evaluate and compare the bonding of flowable resin composites and light-cured resin cements to dental ceramics. METHODS: Grit-blasted zirconia plates were primed with MDP-containing adhesive. Lithium disilicate glasses plates were etched with HF and primed with silane. Two flowable resin composites with high (CM: 75 wt%/62 vol%) and low (BF: 67.3 wt%/47 vol%) filler contents, and two resin cements, again with high (C: 72 wt%/69 vol%) and low (R: 66 wt%/47 vol%) filler contents, were bonded to both types of pretreated ceramics...

STATEMENT OF PROBLEM: Different surface treatments have been applied to zirconia restorations in clinical practice to increase the bond strength between zirconia and cement, but their effect on flexural strength is unknown. PURPOSE: The purpose of this in vitro study was to evaluate the effect of different surface treatments before and after sintering on the flexural strength of zirconia. MATERIAL AND METHODS: Sixty disk-shaped specimens with an initial diameter of 18...

The purpose of this study is to investigate the effects of different root canal irrigation protocols applied to the dentin and artificial aging procedures on the micro pushout bond strength (mPBS) between dentin and hybrid ceramic posts. Seventy-five single-rooted mandibular premolar teeth were divided into 5 groups (Gr1-5). 50 of the teeth were used for the mPBS tests (n = 10), whereas 25 were used for the smear layer examinations (n = 5). Post space were prepared and irrigated with different irrigation-protocols in each group...

OBJECTIVE: To evaluate the microstructure and the influence of applying universal adhesive only versus universal adhesive with additional silane application on shear bond strength (SBS) to four different lithium disilicate ceramic (LDC) materials. MATERIAL AND METHODS: Specimens (n = 240, 1.5 mm thick) cut from four different CAD/CAM materials were polished and etched with 4.5% hydrofluoric (HF) acid according to manufacturers' instructions (20 s: IPS e...

The objective of this study was to evaluate the influence of hydrofluoric acid (HF) and conditioning time on the micro-shear bond strength (µSBS) between dual-cure resin cement and glass-ceramic materials, such as lithium disilicate ceramic (IPS e.max CAD, Ivoclar Vivadent) (EX) and leucite-reinforced ceramic (IPS Empress CAD, Ivoclar Vivadent) (EP), and also a hybrid ceramic (Vita Enamic, Vita Zahnfabrik) (VE). Eighteen sections with 1 mm thickness were cut from each CAD/CAM material and randomly divided into three groups, according to the surface etching time (30 s, 60 s, 90 s)...

Polymer-derived ceramic (PDC) coatings of considerable thickness can offer promising protection for metallic and superalloy substrates against oxidation and corrosion, yet the preparation remains challenging. Here, a SiOC/Al2 O3 /YSZ coating was prepared on a nickel alloy with a spraying method using Al2 O3 and yttria-stabilized zirconia (YSZ) as passive fillers. The thickness can reach up to 97 μm with the optimal mass fraction and particle sizes of the passive fillers. A small or isolated SiOC phase is formed in the coating, which can effectively alleviate the shrinkage and cracking during the pyrolysis...

PURPOSE: To describe the current findings regarding the use of lasers to enhance the bonding properties of zirconia and to enable its debonding. MATERIALS AND METHODS: The PudMed database was searched for literature up to July 2021. The keywords used for zirconia surface treatment were: laser irradiation; zirconia; and bond strength. For ceramic laser debonding, the keywords were: laser irradiation; ceramic; and debonding. RESULTS: A total of 36 studies were included for zirconia surface treatment, and 12 for ceramic laser debonding...

PURPOSE: To evaluate the biaxial flexural strength of different porcelain-to-zirconia thickness ratios and bonding strategies of a stress-free bilayer CAD/CAM ceramic system. MATERIALS AND METHODS: A total of 60 zirconia discs (diameter: 15 mm; thickness: 0.3 or 0.5 mm; n = 30 for each thickness) were divided into six groups (n = 10 each) according to porcelain-to-zirconia ratio and bonding strategy: VM/Zr (control): zirconia discs veneered with a feldspathic ceramic (VM 9, Vita) in 0...

OBJECTIVES: This systematic review aims to investigate the effect of different preparation designs on the marginal fit and fracture strength of ceramic occlusal veneers. MATERIALS AND METHODS: Based on the PICO question and the search terms, an electronic search was performed in Google Scholar, PubMed (MEDLINE), Scopus, Cochrane Library, Web of Science, Science Direct, Wiley, Ovid, and SAGE for articles published up to July 2022. After including English in vitro studies that evaluated posterior ceramic occlusal overlays at the posterior with ceramic restorations by following the PRISMA statement, the extracted data was tabulated...

OBJECTIVES: To evaluate the effect of in-lab simulation of CAD/CAM grinding and intaglio surface treatments on the surface characteristics (topography and roughness) and fatigue behavior of adhesively luted 4YSZ simplified restorations. METHODS: Ceramic discs (Ø = 10 mm, thickness = 1 mm) were randomly allocated into 6 groups considering: "In-lab simulation of CAD/CAM grinding" (ground or polished) and "intaglio surface treatments": Ctrl (without surface treatment), AlOx (aluminum oxide air abrasion) or GLZ (glaze spray application)...

This study aimed to investigate the effect of the thickness of computer aided design-computer aided manufacturing (CAD-CAM) restorative materials on the bond strength of light-polymerized resin cement. Ninety specimens were prepared from three different CAD-CAM materials (a leucite-based glass-ceramic [Empress CAD], a polymer-infiltrated ceramic network [Vita Enamic], and a zirconia-reinforced lithium silicate glass-ceramic [Vita Suprinity]) in different thicknesses (1, 2, and 3 mm). One surface of each specimen was treated by using a single-step self-etching ceramic primer (Monobond Etch & Prime)...

PURPOSE: To analyze the in vitro efficacy of a surface conditioning liquid facilitating ceramic repairs of saliva-contaminated metal-ceramic and all-ceramic restorations. MATERIALS AND METHODS: Specimens constructed from nonprecious alloy (NPA), precious alloy (PA), lithium-disilicate (LD), zirconia (ZI), veneering ceramics for zirconia (VZI), veneering ceramics for lithium-disilicate (VLD), and veneering ceramics for metal alloys (VM) were manufactured (total: n = 168; each material n = 24)...

OBJECTIVE: The objective of this laboratory study was to assess the effect of immediate dentin sealing (IDS) on the fracture strength of teeth restored with ultrathin occlusal veneers made of a polymer-infiltrated ceramic network (PICN - Vita Enamic) with different fissure/cusp thicknesses. METHODS: Forty third molars were identically prepared in the dentin and allocated into four groups (n = 10) according to the fissure/cusp thickness of the occlusal veneers (0...

The success of dental restorations depends mainly on the ability to bond to other filling materials and tooth substances, in order to resist the multitude of forces acting on the bond within the oral cavity. Although the shortcomings of composite resins have been significantly reduced over the past three decades, microleakage due to shrinkage under masticatory loads is unavoidable. In order to overcome such problems, two materials laminated with matched properties can be used to achieve optimum results. The sandwich technique is an approach in which dentine is replaced by glass ionomer cement (GIC), and enamel is replaced by composite resin...